立方氮化硼-碳化钨-钴复合材料制备工艺的改进
Improvement of Preparation of Cubic Boron Nitride Dispersed WC-10Co Composites
摘 要
采用热压烧结方法在温度1 380 ℃、保温60 min、烧结压力30 MPa条件下制备了立方氮化硼(CBN)颗粒体积分数为30%的WC-10Co超细硬质合金复合材料,用化学气相沉积法对立方氮化硼进行了表面镀金属钛膜预处理.对复合材料的组织结构、密度、抗弯强度等性能进行了研究.结果表明：得到的烧结体的相对密度可达到94.2%,弥散立方氮化硼颗粒与超细硬质合金基体之间没有明显的间隙,CBN-WC-10Co复合材料的抗弯强度为750 MPa,WC的平均晶粒尺寸为400 nm;得到了组织结构均匀、力学性能优良的CBN-WC-10Co复合材料.
纳米复合粉末
立方氮化硼
钛膜
WC-10Co
nanocomposite powder
cubic boron nitride(CBN)
titanium film
Abstract
WC-10Co nanocomposite powders were produced by continuous spray pyrolysis & carbonization technology and Ti-coated cubic boron nitride(CBN) was prepared by using chemical vapor deposition.Hot-pressing sintering technology was used to prepare CBN-WC-10Co composites at 1 380 ℃ under 30 MPa for 60 minutes.The microstructure,density,transverse rupture strength (TRS),and bonding conditions between CBN and ultrafine WC-10Co matrix were studied.The average grain size of WC grains is 400 nm,TRS of CBN-WC-10Co composites is more than 750 MPa and the relative density is 94.2%.CBN-WC-10Co composites with homogeneous microstructure and good mechanical properties are obtained.
中图分类号 TG146.4
所属栏目
基金项目 武汉市攻关项目(20041003068-04);教育部科学技术重点研究项目(105123)
收稿日期 2006/4/3
修改稿日期 2006/6/22
网络出版日期
作者单位点击查看
备注史晓亮(1974-),男,黑龙江佳木斯人,副研究员,博士.
引用该论文: SHI Xiao-liang,YANG Hua,SHAO Gang-qin,DUAN Xing-long,ZHOU Fu-rong,SUN Peng. Improvement of Preparation of Cubic Boron Nitride Dispersed WC-10Co Composites[J]. Materials for mechancial engineering, 2007, 31(4): 71～73
史晓亮,杨华,邵刚勤,段兴龙,周芙蓉,孙鹏. 立方氮化硼-碳化钨-钴复合材料制备工艺的改进[J]. 机械工程材料, 2007, 31(4): 71～73
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】史晓亮.金刚石-硬质合金复合齿及其钻头的研究[D].武汉:中国地质大学,2003.
【2】Benko E,Klimczyk P,Mackiewicz S,et al.CBN–Ti3SiC2 composites[J].Diamond and Related Materials,2004,13(1):521-525.
【3】王明智,臧建兵,王艳辉.立方氮化硼表面镀Ti及其与金属粘结剂的作用[J].中国有色金属学报,1997,7(2):104-106.
【4】孙剑飞,张法明,沈军.纳米W-Co硬质合金的制备[J].稀有金属与硬质合金,2002(1):33-37.
【5】解迎芳,王兴庆,陈立东,等.纳米硬质合金的放电等离子烧结[J].硬质合金,2003,20(3):138-142.
【6】岳明,王公平,张久兴,等.一种新型NdFeB磁性材料的放电等离子烧结[J].稀有金属材料与工程,2003,32(10):844-547.
【7】刘科高,张久兴,路清梅,等.机械合金化和放电等离子烧结制备纳米CoSb3热电材料[J].稀有金属材料与工程,2004,33(3):329-332.
【8】韩斌,翁履谦,黄栋生.WC-Co硬质合金的真空气压烧结[J].稀有金属材料与工程,1996,25(3):34-36.
【9】刘寿荣,刘 宜.硬质合金矫顽磁力和硬度之间的关系[J].稀有金属材料与工程,1995,24(5):58-61.
【10】张玉华,张纪生.纳米WC-Co硬质合金[J].稀有金属材料与工程,1995,24(2):18-21.
【11】杜国臣.聚晶立方氮化硼刀具的选用[J].机械制造,2004,42(1):61-63.
【12】杜国臣.PCBN刀具及其在切削加工中的应用[J].潍坊学院学报,2004,4(2):39-50.
【13】Shi X L,Shao G Q,Duan X L,et al.Mechanical properties,phases and microstructure of ultrafine hardmetals prepared by WC-6.29Co nanocrystalline composite powder[J].Materials Science and Engineering A,2005,392(1/2):335-339.
【14】张立学,金志浩,Miyamoto Yoshinari.金刚石颗粒弥散WC-Co复合物的烧结及其韧化[J].复合材料学报,2004,21(1):51-55.
【2】Benko E,Klimczyk P,Mackiewicz S,et al.CBN–Ti3SiC2 composites[J].Diamond and Related Materials,2004,13(1):521-525.
【3】王明智,臧建兵,王艳辉.立方氮化硼表面镀Ti及其与金属粘结剂的作用[J].中国有色金属学报,1997,7(2):104-106.
【4】孙剑飞,张法明,沈军.纳米W-Co硬质合金的制备[J].稀有金属与硬质合金,2002(1):33-37.
【5】解迎芳,王兴庆,陈立东,等.纳米硬质合金的放电等离子烧结[J].硬质合金,2003,20(3):138-142.
【6】岳明,王公平,张久兴,等.一种新型NdFeB磁性材料的放电等离子烧结[J].稀有金属材料与工程,2003,32(10):844-547.
【7】刘科高,张久兴,路清梅,等.机械合金化和放电等离子烧结制备纳米CoSb3热电材料[J].稀有金属材料与工程,2004,33(3):329-332.
【8】韩斌,翁履谦,黄栋生.WC-Co硬质合金的真空气压烧结[J].稀有金属材料与工程,1996,25(3):34-36.
【9】刘寿荣,刘 宜.硬质合金矫顽磁力和硬度之间的关系[J].稀有金属材料与工程,1995,24(5):58-61.
【10】张玉华,张纪生.纳米WC-Co硬质合金[J].稀有金属材料与工程,1995,24(2):18-21.
【11】杜国臣.聚晶立方氮化硼刀具的选用[J].机械制造,2004,42(1):61-63.
【12】杜国臣.PCBN刀具及其在切削加工中的应用[J].潍坊学院学报,2004,4(2):39-50.
【13】Shi X L,Shao G Q,Duan X L,et al.Mechanical properties,phases and microstructure of ultrafine hardmetals prepared by WC-6.29Co nanocrystalline composite powder[J].Materials Science and Engineering A,2005,392(1/2):335-339.
【14】张立学,金志浩,Miyamoto Yoshinari.金刚石颗粒弥散WC-Co复合物的烧结及其韧化[J].复合材料学报,2004,21(1):51-55.
相关信息