超高压压缩机填料盘裂纹产生原因分析
Failure Analysis of Stuffing Box of Hypercompressor
摘 要
对产生裂纹的填料盘进行了失效分析,通过拉梅公式和有限元分析软件对填料盘简化模型进行了受力分析.结果表明:材料成分和显微组织均符合要求;裂纹起源于输油孔的侧壁;填料盘的失效模式为疲劳失效,内压在填料盘内部输油孔上产生的应力集中导致了填料盘的疲劳失效.适当增加输油孔到填料盘内环的距离可以预防裂纹的产生.
疲劳
应力分析
失效分析
stuffing box
fatigue
stress analysis
failure analysis
Abstract
Base on failure analysis and stress distribution analysis of the stuffing box using the Lame Formula and software ANSYS in predigested model,it is found that the composition of the material accorded with the requirement for stuffing box,and the microstructure with few impurity was qualified.The fracture of stuffing box was caused by fatigue,which resulted from the maximum stress concentration on the centripetal border of the oil hole.Increasing the distance from oil hole to inner annulus of the stuffing box can prevent the fatigue.
中图分类号 TG111.8
所属栏目
基金项目
收稿日期 2006/5/29
修改稿日期 2006/9/20
网络出版日期
作者单位点击查看
备注吕连忠(1981-),男,山东潍坊人,硕士研究生.
引用该论文: Lv Lian-zhong,WAN Lei,ZHANG Zheng,WANG Feng-jiang,GE Fen-li. Failure Analysis of Stuffing Box of Hypercompressor[J]. Materials for mechancial engineering, 2007, 31(4): 74～76
吕连忠,万蕾,张峥,王凤江,葛粉利. 超高压压缩机填料盘裂纹产生原因分析[J]. 机械工程材料, 2007, 31(4): 74～76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】《工程材料实用手册》编辑委员会.工程材料实用手册(第1卷)[M].北京:中国标准出版社,2002.
【2】徐芝纶.弹性力学简明教程[M].北京:高等教育出版社,2002.
【3】洪庆章.ANSYS教学范例[M].北京:中国铁道出版社,2002.
【4】钟群鹏,田永江.失效分析基础[M].北京:机械工业出版社,1991.
【2】徐芝纶.弹性力学简明教程[M].北京:高等教育出版社,2002.
【3】洪庆章.ANSYS教学范例[M].北京:中国铁道出版社,2002.
【4】钟群鹏,田永江.失效分析基础[M].北京:机械工业出版社,1991.
相关信息