GCr15SiMn钢轴承套圈开裂原因分析
Failure Analysis on Cracking of a GCr15SiMn Steel Bearing Terrule
摘 要
采用光学显微镜、扫描电镜等检测分析手段,对GCr15SiMn钢轴承套圈开裂原因进行了分析.结果表明：引起套圈开裂的主要原因是由于锻造比不够,始锻和终锻温度偏高,造成套圈组织中存在碳化物偏析以及碳化物呈网状分布,使材料的脆性显著增大.在淬火过程中,由于热应力和相变应力的作用导致轴承套圈萌发裂纹,进而在磨削工序外力作用下裂纹扩展而失效.
轴承套圈
开裂
失效分析
GCr15SiMn steel
bearing terrule
crack
failure analysis
Abstract
The reason on cracking failure of GCr15SiMn steel bearing terrule had been analyzed by OM,SEM and EPMA etc.The primary reason of terrule cracking is originated from carbide aliquation and reticulation distributing of metallurgical structure because of low forging ratio and high beginning forging and ending forging temperature,which increased brittleness markedly.During quenching process,the cracks are facilitated by such factors as heat stress and phase transition stress,then the cracks are extended by procedure external grinding force,which induced terrule failure.
中图分类号 TG162.71
所属栏目
基金项目
收稿日期 2006/3/20
修改稿日期 2006/7/8
网络出版日期
作者单位点击查看
备注邹龙江(1963-),男,辽宁瓦房店人,副教授,博士研究生.
引用该论文: ZOU Long-jiang,GAO Lu-si,WANG Lan-fang. Failure Analysis on Cracking of a GCr15SiMn Steel Bearing Terrule[J]. Materials for mechancial engineering, 2007, 31(5): 52～54
邹龙江,高路斯,王兰芳. GCr15SiMn钢轴承套圈开裂原因分析[J]. 机械工程材料, 2007, 31(5): 52～54
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】全国滚动轴承标准化技术委员会.滚动轴承用材料和热处理卷(上)[M].北京:中国标准出版社,2003:5-57.
【2】全国滚动轴承标准化技术委员会.滚动轴承用材料和热处理卷(下)[M].北京:中国标准出版社,2003:4-16.
【3】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998:27-33.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2005:157-164.
【5】王焕庭,李茅华,徐善国.机械工程材料[M].大连:大连理工大学出版社,2000:101-102.
【6】戚正风.金属热处理[M].北京:机械出版社,2004:102-105.
【7】卢淑君,仇亚军,梁 华.滚动轴承零件的裂纹分析[J].轴承,2001(8):8-24.
【2】全国滚动轴承标准化技术委员会.滚动轴承用材料和热处理卷(下)[M].北京:中国标准出版社,2003:4-16.
【3】崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998:27-33.
【4】张栋,钟培道,陶春虎,等.失效分析[M].北京:国防工业出版社,2005:157-164.
【5】王焕庭,李茅华,徐善国.机械工程材料[M].大连:大连理工大学出版社,2000:101-102.
【6】戚正风.金属热处理[M].北京:机械出版社,2004:102-105.
【7】卢淑君,仇亚军,梁 华.滚动轴承零件的裂纹分析[J].轴承,2001(8):8-24.
相关信息