耐候钢形变奥氏体的连续冷却转变行为
The Continuous Cooling Austenite Transition of the Weathering Steel Deformation
摘 要
采用热膨胀法结合硬度测试得到耐候钢未变形和变形奥氏体的连续冷却转变曲线;用光学显微镜和透射电镜分析了冷却速率、变形条件对显微组织的影响.结果表明:变形奥氏体与未变形的相比,铁素体+珠光体相变区向左上方移动,获得铁素体+珠光体的临界冷速增大;变形奥氏体的位错缠结抑制了贝氏体长大,细化了相变后的显微组织;在冷速大于15 ℃/s时,获得板条状贝氏体,第二相是渗碳体;在冷速5~10 ℃/s的范围内获得粒状贝氏体,第二相为基体上分布的马氏体/奥氏体岛.
奥氏体转变
连续冷却转变曲线
weathering steel
austenite transformation
continuous cooling transformation curve
Abstract
The continuous cooling transformation (CCT) diagrams of austenite non-deformation and deformed at 950 ℃ were constructed by means of a combined dilatometry and Vickers-hardness measurement for a weathering steel.Optical microscope and TEM were employed to investigate the influence of cooling rate,deformation process on the transformation behavior and microstructure.Results show that the deformation promotes the area of ferrite move towards top left corner,leading to the increase of critical cooling rate obtained ferrite plus pearlite.The deformation on austenite stifled the growth of bainitic ferrite by tangled dislocations resulting the refinement of microstructure.Lath-like microstructure observed at the cooling rate above 15 ℃/s mainly is revealed to consist of bainitic-ferrite with cementite.Granular microstructure observed at the cooling rate ranging from 5-10 ℃/s is characterized to be martensite-ausenite constituent islands.
中图分类号 TG115.21
所属栏目
基金项目 国家二期973计划资助项目(2004CB619101)
收稿日期 2006/10/18
修改稿日期 2007/3/2
网络出版日期
作者单位点击查看
备注吴红艳(1976-),女,辽宁鞍山人,博士研究生.
引用该论文: WU Hong-yan,SHEN Kai-zhao,ZHA Chun-he,DU Lin-xiu,LIU Xiang-hua,WANG Guo-dong. The Continuous Cooling Austenite Transition of the Weathering Steel Deformation[J]. Materials for mechancial engineering, 2007, 31(5): 72～75
吴红艳,沈开照,查春和,杜林秀,刘相华,王国栋. 耐候钢形变奥氏体的连续冷却转变行为[J]. 机械工程材料, 2007, 31(5): 72～75
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王传雅,戚正风.耐候钢的化学成分和性能[J].特殊钢,1997,18(1):13-19.
【2】王庆山.黑色金属强度-硬度换算经验公式[J].理化检验-物理分册,1995,31(2):39-41.
【3】Bramfitt B L,Speer J G.A perspective on the morphology of bainite[J].Metallurgical Transactions A,1990,21A(4):817-829.
【4】乔兵,王秉新,刘相华.奥氏体状态对Mn-Cr齿轮钢连续冷却相变组织的影响[J].特殊钢,2005,26(5):25-27.
【5】Biss V,Cryderman R L.Martensite and retained austenite in hot-rolled lower carbon bainitic steels[J].Metall Trans A,1971,2:2267-2276.
【2】王庆山.黑色金属强度-硬度换算经验公式[J].理化检验-物理分册,1995,31(2):39-41.
【3】Bramfitt B L,Speer J G.A perspective on the morphology of bainite[J].Metallurgical Transactions A,1990,21A(4):817-829.
【4】乔兵,王秉新,刘相华.奥氏体状态对Mn-Cr齿轮钢连续冷却相变组织的影响[J].特殊钢,2005,26(5):25-27.
【5】Biss V,Cryderman R L.Martensite and retained austenite in hot-rolled lower carbon bainitic steels[J].Metall Trans A,1971,2:2267-2276.
相关信息