20钢多元共渗后的耐腐蚀性能
Corrosion Resistance of Multi-element Penetrated 20 Steel
摘 要
采用低温气体多元共渗技术在20钢表面同时渗入碳、氮、氧三种元素,利用X射线衍射仪(XRD)测定了渗层的相组成;另外测试了渗层在浓度为1.0 mol/L HCl溶液中的耐蚀性.结果表明:渗层以氧化物、氮化物和碳化物为主,且氮化物居多,其腐蚀速率明显低于基体材料的腐蚀速率.
多元共渗
耐蚀性
20 steel
multi-element penetration
corrosion resistance
Abstract
Corrosion performance of 20 steel was improved by low temperature gas multi-element penetration technique.Carbon,nitrogen and oxygen were infiltrated into the material.The phase constituents of the alloying layer were investigated by XRD.The corrosion resistance of the penetrated layer and original material was compared by electrochemical method in 1.0 mol/L HCl solution.The results show that the penetrated layer consists of oxide,nitride and carbide.Among them the nitride is predominant.In comparison with the original material,the penetrated layer has much better corrosion resistance and lower corrosion rate.
中图分类号 TG147.445
所属栏目
基金项目
收稿日期 2006/10/17
修改稿日期 2007/8/14
网络出版日期
作者单位点击查看
备注周海(1957-),男,广东开平人,副教授.
引用该论文: ZHOU Hai,YANG Ying-ge,CHEN Fei,WAN Han-cheng,XI Ming. Corrosion Resistance of Multi-element Penetrated 20 Steel[J]. Materials for mechancial engineering, 2007, 31(8): 49～50
周海,杨英歌,陈飞,万汉城,奚明. 20钢多元共渗后的耐腐蚀性能[J]. 机械工程材料, 2007, 31(8): 49～50
被引情况:
【1】王小红,闫静,陈小时,任呈强,黄本生, "N80钢表面碳、氮、氧、铬共渗层的组织和耐腐蚀性能",机械工程材料 34, 54-56(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杨川.碳素结构钢多元共渗后的微观组织结构与抗蚀性的关系[J].材料保护,2004,37(11):42-43.
【2】杨川.超厚硼铝共渗层的研究[J].金属热处理学报,1995,16(3):60-63.
【3】郝少祥,谭 萍.20钢固体渗铝的试验研究[J].河南科学,2004,22(6):783-785.
【4】梁成浩,隋洪艳.TiNiCu形状记忆合金的耐蚀性研究[J].稀有金属材料与工程,2001,30(2):93-96.
【5】戚正风.金属热处理原理[M].北京:机械工业出版社,1987.
【6】刘永辉.电化学测试技术[M].北京:北京航空出版社,1987.
【2】杨川.超厚硼铝共渗层的研究[J].金属热处理学报,1995,16(3):60-63.
【3】郝少祥,谭 萍.20钢固体渗铝的试验研究[J].河南科学,2004,22(6):783-785.
【4】梁成浩,隋洪艳.TiNiCu形状记忆合金的耐蚀性研究[J].稀有金属材料与工程,2001,30(2):93-96.
【5】戚正风.金属热处理原理[M].北京:机械工业出版社,1987.
【6】刘永辉.电化学测试技术[M].北京:北京航空出版社,1987.
相关信息