飞机发动机减速器支撑杆加工裂纹原因分析
Analysis of Process Crack on Support Part for Engine of Aircraft
摘 要
飞机发动机减速器支撑杆在加工过程中易产生微裂纹,通过显微组织检验、断口形貌观察、微区成分分析以及含氢量测定和模拟焊接试验等方法对其裂纹产生的原因进行了分析.结果表明:减速器支撑杆产生微裂纹的主要原因是焊接时采用的保护气(氩气)中水分超过标准规定37.7倍,在焊缝热影响区造成增氢,导致氢致延迟裂纹的产生.
焊接
氢致延迟裂纹
失效分析
tiny crack
welding
hydrogen embrittlement crack
failure analysis
Abstract
Tiny crack appeared on the support part of the aircraft engine during the processing.Through microstructure analysis,fracture side analysis,hydrogen contain measure and welding test,the reason of the tiny crack appearing was analyzed.The results show that tiny crack main by using the unqualified protect gas(Ar)during welding could cause the increasing hydrogen contain in the weld area,created the hydrogen embrittlement crack.
中图分类号 TG146.1
所属栏目
基金项目
收稿日期 2006/12/26
修改稿日期 2007/3/30
网络出版日期
作者单位点击查看
备注包俊成(1965-),男,内蒙古海拉尔人,教授级高工,硕士.
引用该论文: BAO Jun-cheng,WANG Zhi-qi,ZHAO Jie,LIU Chang-ying. Analysis of Process Crack on Support Part for Engine of Aircraft[J]. Materials for mechancial engineering, 2007, 31(10): 67～69
包俊成,王志奇,赵捷,刘长英. 飞机发动机减速器支撑杆加工裂纹原因分析[J]. 机械工程材料, 2007, 31(10): 67～69
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】涂铭旌,鄢文彬.机械零件失效分析与预防[M].北京:高等教育出版社,1993.
【2】陈伯蠡.焊接工程缺欠分析与对策[M].北京:机械工业出版社,1990.
【3】褚武扬.氢损伤和滞后断裂[M].北京:冶金工业出版社,1988.
【2】陈伯蠡.焊接工程缺欠分析与对策[M].北京:机械工业出版社,1990.
【3】褚武扬.氢损伤和滞后断裂[M].北京:冶金工业出版社,1988.
相关信息