Effects of Heat Treatment Process on Properties of 1Cr13 Stainless Steel Containing Cu and Mo
摘 要
研究了热处理工艺对含铜钼1Cr13马氏体不锈钢抗菌性、耐腐蚀性和硬度的影响.采用均匀设计法设计热处理工艺,并用回归方程分析了试验结果.结果表明:当1Cr13Cu3Mo钢经1 200 ℃×15 min固溶、550 ℃×1 h时效后,其硬度和抗菌率具有最大值,硬度达到40.6 HRC,抗菌率为100%;该钢在不同介质中的腐蚀速率随时间的增加而减小,最后趋零.
Abstract
The effects of heat treatment process on antibacterial property,corrosion resistance and hardness of 1Cr13 martensite stainless steel containing Cu and Mo were studied.Heat treatment process was designed by uniformity design and the results were analyzed by regression equations.The results show that antibacterial rate and hardness have maximum values after solution at 1 200 ℃×15 min and aging at 550 ℃×1 h and hardness is 40.6 HRC,antibacterial is 100%.The corrosion rate of 1Cr13Cu3Mo decrease with time to zero.
中图分类号 TG142.71
所属栏目
基金项目
收稿日期 2006/11/14
修改稿日期 2007/1/30
网络出版日期
作者单位点击查看
备注王小丽(1982-),女,四川江油人,硕士研究生.
引用该论文: WANG Xiao-li,ZHANG Xiao-chen,PANG Zhan-jun,ZHANG Wei-qiang,ZHU Hong-fei. Effects of Heat Treatment Process on Properties of 1Cr13 Stainless Steel Containing Cu and Mo[J]. Materials for mechancial engineering, 2007, 31(12): 59~61
王小丽,张晓晨,庞占军,张伟强,朱宏飞. 热处理工艺对含铜钼1Cr13不锈钢性能的影响[J]. 机械工程材料, 2007, 31(12): 59~61
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】熊娟,许伯藩,但智钢,等.铜离子注入不锈钢中的剂量与抗菌性[J].材料热处理学报,2004,25(2):45-47.
【2】但智钢,倪红卫,许伯藩.铜离子注入马氏体不锈钢的抗菌性能研究[J].功能材料,2004,35(4):527-529.
【3】张伟,李宁,胥永刚.3Cr13Cu3马氏体不锈钢抗菌性能[J].特殊钢,2004,25(2):27-28.
【4】张伟,李宁,胥永刚.热处理对含铜3Cr13马氏体不锈钢抗菌性能的影响[J].金属热处理,2004,29(8):21-23.
【5】方开泰.均匀设计与均匀设计表[M].北京:科学出版社,1994:115.
【6】杨志勇,李文辉,林师焱.抗菌不锈钢材料的开发[J].金属功能材料,2000,7(4):1-7.
【7】刘秀晨,安成强.金属腐蚀学[M].第1版.北京:国防工业出版社,2002.
【2】但智钢,倪红卫,许伯藩.铜离子注入马氏体不锈钢的抗菌性能研究[J].功能材料,2004,35(4):527-529.
【3】张伟,李宁,胥永刚.3Cr13Cu3马氏体不锈钢抗菌性能[J].特殊钢,2004,25(2):27-28.
【4】张伟,李宁,胥永刚.热处理对含铜3Cr13马氏体不锈钢抗菌性能的影响[J].金属热处理,2004,29(8):21-23.
【5】方开泰.均匀设计与均匀设计表[M].北京:科学出版社,1994:115.
【6】杨志勇,李文辉,林师焱.抗菌不锈钢材料的开发[J].金属功能材料,2000,7(4):1-7.
【7】刘秀晨,安成强.金属腐蚀学[M].第1版.北京:国防工业出版社,2002.
相关信息