304不锈钢的超高周疲劳性能
Fatigue Life in Very High Cycle Range of 304 Stainless Steel
摘 要
采用超声疲劳试验技术对304不锈钢超高周疲劳性能进行了研究,并用扫描电镜对疲劳断口进行了分析.结果表明:304不锈钢在105~1010周次范围内的S-N曲线呈阶梯型下降趋势;在106~108周次出现平台,平台对应应力幅约为200 MPa;在平台应力以下,108周次以上超高周范围304不锈钢仍然发生疲劳断裂,不存在传统意义的疲劳强度;高周和超高周断裂试样的裂纹主要从试样表面萌生.
S-N曲线
304不锈钢
ultrasonic fatigue
S-N curve
304 stainless steel
Abstract
Fatigue behavior of 304 stainless steel was studied with the ultrasonic fatigue testing,and with scanning electron examination of the fatigue crack fracture surface.The curve of 304 stainless steel exhibites the stepwise shape and the platform appeares in teh range of 106-108 cycles.The stress of platform is about 200 MPa fatigue fracture of 304 stainless steel occurred above 108 cycles and below the stress platform.Most of the fatigue cracks initiated from the surface of specimen.
中图分类号 TG146.1
所属栏目
基金项目 西南交通大学科学发展基金资助项目(2005A10)
收稿日期 2007/3/15
修改稿日期 2007/4/26
网络出版日期
作者单位点击查看
备注张真源(1980-),男,四川德阳人,硕士研究生.
引用该论文: ZHANG Zhen-yuan,WANG Hong. Fatigue Life in Very High Cycle Range of 304 Stainless Steel[J]. Materials for mechancial engineering, 2008, 32(1): 79～80
张真源,王弘. 304不锈钢的超高周疲劳性能[J]. 机械工程材料, 2008, 32(1): 79～80
被引情况:
【1】燕怒,韩晓琪,余泳华,游敏,彭文杰, "GH4169镍基高温合金的超高周疲劳性能",机械工程材料 40, 9-12(2016)
【2】董鑫,李培源,王旭,高潮,程礼, "腐蚀对TC17钛合金超高周疲劳性能的影响",机械工程材料 38, 76-79(2014)
【3】陈凯,杜东海,陆辉,张乐福,徐雪莲,石秀强,孟凡江,鲍一晨,刘晓强, "用直流电压降法研究316LN不锈钢的疲劳裂纹扩展行为",机械工程材料 40, 7-10(2016)
【4】龙远强,邓建新,周后明,易斌, "微织构自润滑刀具干切削0Cr18Ni9奥氏体不锈钢的切削性能",机械工程材料 39, 75-79(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】程林.换热器内流体诱发振动[M].北京:科学出版社,1995.
【2】薛红前,陶 华.超声疲劳试样设计[J].航空学报,2004,25(4):12-16.
【3】鲁连淘,张卫华.金属材料超高周疲劳研究综述[J].机械强度,2005,27(3):388-394.
【4】王清远.超高强度钢十亿周疲劳研究[J].机械强度,2002,24(1):81-83.
【2】薛红前,陶 华.超声疲劳试样设计[J].航空学报,2004,25(4):12-16.
【3】鲁连淘,张卫华.金属材料超高周疲劳研究综述[J].机械强度,2005,27(3):388-394.
【4】王清远.超高强度钢十亿周疲劳研究[J].机械强度,2002,24(1):81-83.
相关信息