Tensile Behaviors of IC10 Alloy at High Temperatures
摘 要
利用力学测试与模拟试验机测得了IC10合金在很宽的温度范围(25~900℃)和不同应变速率(10-5~10-2 s-1)下的应力-应变曲线,对曲线进行了分析;用扫描电子显微镜对试样的断口进行了分析.结果表明:室温下IC10合金的流变应力对应变速率不太敏感,而在900℃下对应变速率非常敏感;比较各温度下材料的屈服强度可以发现,当温度低于(含)800℃时,IC10合金的力学性能与室温下相当,而在更高的温度(900℃)下力学性能有所下降;在低于(含)800℃时断口主要以穿晶断裂为主,在900℃下主要为韧窝聚集型断裂,随着温度的增加,断口上韧窝更大、更深、更多.
Abstract
The tensile experiments were conduct over a wide range of temperatures (25-900℃) and strain rates (10-5-10-2 s-1) on a material testing system to investigate the flow behaviors of alloy IC10.The anomalous temperature dependence of yield stress was also investigated.The characters of fractures at different temperatures were studied with the aid of scanning electron microscopy.The stress-strain curves revealsed that the flow behaviors were sensitive to strain rates at 900℃,but not at room temperature.When the temperature was below (including) 800℃,the fracture was transgranular cracking mixed with a few dimpled and intergranular fracture.The fracture was ductile cracking at 900℃.A close comparison among the fractures under various conditions revealed that the number of the ductile dimples increased with the temperature,and the dimples at evaluated temperature were deeper and larger.
中图分类号 TB125 TB35 TB741
所属栏目
基金项目
收稿日期 2007/5/19
修改稿日期 2007/6/6
网络出版日期
作者单位点击查看
备注张宏建(1980-),男,江苏如皋人,博士研究生.
引用该论文: ZHANG Hong-jian,WEN Wei-dong,CUI Hai-tao,TAO Yong-chang. Tensile Behaviors of IC10 Alloy at High Temperatures[J]. Materials for mechancial engineering, 2008, 32(3): 52~56
张宏建,温卫东,崔海涛,陶永昌. IC10合金的高温拉伸性能[J]. 机械工程材料, 2008, 32(3): 52~56
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐颂波.新一代高温结构材料——金属间化合物Ni3Al[J].上海有色金属,1997,18(2):88-92.
【2】Han Y F,Xing Z P,Chaturvedi M C.Development and engineering application of a ds cast Ni3Al alloy IC6[C]//Nathal MV,Darolia R,Liu CT,et al.The Second International Symposium on Structural Intermetallics.Warrendale,Pennsylvania:[s.n]1997:713-719.
【3】Hiroyuki Senba,Masaaki Igarashi.Creep deformation behavior and microstructure evolution of NiAl/Ni3Al multiphase alloys[C]//Nathal MV,Darolia R,Liu CT,et al.The Second International Symposium on Structural Intermetallics.Warrendale,Pennsylvania:[s.n]1997:595-604.
【4】Lang Fengqun,Toshio Narita.Improvement in oxidation resistance of a Ni3Al-based superalloy IC6 by rhenium-based diffusion barrier coatings[J].Intermetallics,2007,15:599-606.
【5】赵希宏,黄朝晖,谭永宁,等.新型Ni3Al基定向高温合金IC10[J].航空材料学报,2006,16(3):20-24.
【6】何玉怀,刘绍伦.Ni3Al合金热/机械疲劳裂纹扩展行为研究[J].材料工程,2000(11):13-14.
【7】毛唯,李哓红,程耀永,等.IC10 与GH3039高温合金的真空纤焊[J].焊接,2004(7):17-20.
【8】侯金保,魏友辉,张蕾.Ni3Al基合金TLP扩散焊接头性能[J].航空材料学报,2006,26(3):329-330.
【9】叶雷,李哓红,毛唯.不同中间层合金对IC10合金的连接[J].航空材料学报,2006,26(3):319-320.
【2】Han Y F,Xing Z P,Chaturvedi M C.Development and engineering application of a ds cast Ni3Al alloy IC6[C]//Nathal MV,Darolia R,Liu CT,et al.The Second International Symposium on Structural Intermetallics.Warrendale,Pennsylvania:[s.n]1997:713-719.
【3】Hiroyuki Senba,Masaaki Igarashi.Creep deformation behavior and microstructure evolution of NiAl/Ni3Al multiphase alloys[C]//Nathal MV,Darolia R,Liu CT,et al.The Second International Symposium on Structural Intermetallics.Warrendale,Pennsylvania:[s.n]1997:595-604.
【4】Lang Fengqun,Toshio Narita.Improvement in oxidation resistance of a Ni3Al-based superalloy IC6 by rhenium-based diffusion barrier coatings[J].Intermetallics,2007,15:599-606.
【5】赵希宏,黄朝晖,谭永宁,等.新型Ni3Al基定向高温合金IC10[J].航空材料学报,2006,16(3):20-24.
【6】何玉怀,刘绍伦.Ni3Al合金热/机械疲劳裂纹扩展行为研究[J].材料工程,2000(11):13-14.
【7】毛唯,李哓红,程耀永,等.IC10 与GH3039高温合金的真空纤焊[J].焊接,2004(7):17-20.
【8】侯金保,魏友辉,张蕾.Ni3Al基合金TLP扩散焊接头性能[J].航空材料学报,2006,26(3):329-330.
【9】叶雷,李哓红,毛唯.不同中间层合金对IC10合金的连接[J].航空材料学报,2006,26(3):319-320.
相关信息