Fe3Al金属间化合物多孔材料的孔隙特征
Porosity of Fe3Al Intermetallic Porous Materials
摘 要
通过在Fe3Al粉末中添加挥发性造孔剂,利用粉末冶金技术制备了Fe3Al金属间化合物多孔材料,研究了其孔隙特性和成孔机理,并通过计算分析了孔隙比表面积及平均有效孔径.结果表明:随着Fe3Al多孔材料的开孔隙率不断增加,材料比表面积不断减小,平均有效孔径不断增大;通过近似计算,得出添加25%聚甲基丙烯酸甲酯(PMMA)的试样平均有效孔径达到21.6 μm,比表面积超过2 000 cm2·cm-3;Fe3Al多孔材料内部大孔壁上的微孔可以帮助造孔剂顺利挥发排除,也可以增加Fe3Al多孔材料比表面积和渗透性能.
多孔材料
孔隙率
渗透性
Fe3Al intermetallics
porous material
porosity
penetrability
Abstract
The Fe3Al intermetallic porous materials were fabricated by means of powder metallurgy process.The properties of pores and the pore-forming mechanism were studied.The specific area and average effective pore radius were analyzed by simulation.The results show that with the increase of open porosity,the specific area decreased and the average effective pore radius increased,the average effective pore radius and specific area of 25wt%PMMA are 21.6 μm and more than 2 000 cm2·cm-3 respectively.The very small pores on the wall of large pores would help pore forming agents to volatilize and play a role in the increase of the penetrability and specific area.
中图分类号 TG146.2
所属栏目
基金项目 上海市科委纳米专项资金资助项目(0452nm036)
收稿日期 2007/7/2
修改稿日期 2007/9/26
网络出版日期
作者单位点击查看
备注陈斌(1983-),男,上海人,硕士研究生.
引用该论文: CHEN Bin,PANG Hou-jun,ZHANG Xiu-qing,YE Yi-fu. Porosity of Fe3Al Intermetallic Porous Materials[J]. Materials for mechancial engineering, 2008, 32(5): 33～37
陈斌,庞厚君,张修庆,叶以富. Fe3Al金属间化合物多孔材料的孔隙特征[J]. 机械工程材料, 2008, 32(5): 33～37
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】John Banhart.Manufacture,characterisation and application of cellular metals and metal foams[J].Progress in Materials Science,2001,46:559-632.
【2】LIU Peisheng,YU Bing,HU Anmin.Techniques for the preparation of Porous Metals[J].J Mater Sci Technol,2002,18(4):299-305.
【3】汤慧萍,谈萍.烧结金属多孔材料研究进展[J].稀有金属材料与工程,2006,35(2):428-432.
【4】张永刚,韩雅芳,陈国良,等.金属间化合物结构材料[M].北京:国防工业出版社,2001:857-902.
【5】刘培生.多孔材料孔率的测试方法[J].钛工业进展,2005,22(6):34-37.
【6】宝鸡有色金属研究所.粉末冶金多孔材料(下册)[M].北京:冶金工业出版社,1979:2-51.
【7】王文军.落锤法测定焦炭强度[C]//中国焦化年会论文集.北京,2000:322-327.
【8】伊达贤治,中井真澄.多孔烧结金属及其过滤器,以及制备该烧结金属的方法:日本,03147658.9[P].2004-03-03.
【9】黄培云.粉末冶金原理[M].北京:冶金工业出版社,1982:24-50.
【2】LIU Peisheng,YU Bing,HU Anmin.Techniques for the preparation of Porous Metals[J].J Mater Sci Technol,2002,18(4):299-305.
【3】汤慧萍,谈萍.烧结金属多孔材料研究进展[J].稀有金属材料与工程,2006,35(2):428-432.
【4】张永刚,韩雅芳,陈国良,等.金属间化合物结构材料[M].北京:国防工业出版社,2001:857-902.
【5】刘培生.多孔材料孔率的测试方法[J].钛工业进展,2005,22(6):34-37.
【6】宝鸡有色金属研究所.粉末冶金多孔材料(下册)[M].北京:冶金工业出版社,1979:2-51.
【7】王文军.落锤法测定焦炭强度[C]//中国焦化年会论文集.北京,2000:322-327.
【8】伊达贤治,中井真澄.多孔烧结金属及其过滤器,以及制备该烧结金属的方法:日本,03147658.9[P].2004-03-03.
【9】黄培云.粉末冶金原理[M].北京:冶金工业出版社,1982:24-50.
相关信息