BTi6431S高温钛合金盒形件超塑性成型工艺
Superplastic Forming Technology of Box-shaped Piece of High-temperature Titanium Alloy BTi6431S
摘 要
采用速度突变法对BTi6431S钛合金进行了高温超塑性拉伸试验,得到了其超塑性特征参数;在此基础上用Marc2003有限元软件模拟了BTi6431S板料盒形件的超塑性成型过程,获得了用于成型工艺的优化加载曲线,并进行了超塑性成型试验.结果表明：BTi6431S钛合金有较好的高温超塑性,在865 ℃下,应变速率为1.5×10-4 s-1时,应变速率敏感指数m=0.5,伸长率为306.1%,流变应力为71.2 MPa;在经过优化的加载路径下可以成型出质量合格的复杂盒形件,其厚度的预测结果与试验结果吻合良好.
超塑性成型
有限元模拟
high-temperature titanium alloy
superplastic forming
FEM simulation
Abstract
The superplastic parameters of titanium alloy BTi6431S was obtained using sudden rate changing technique in superplastic temperature range.On the basis of tensile test,the formability of titanium alloy BTi6431S was analyzed and the superplastic forming of box-shaped piece of BTi6431S sheet was simulated with the aid of finite element analysis software Marc2003.Then,the process of superplastic forming was tested.The results show that the titanium alloy BTi6431S has good superplasticity with m=0.5,δ=306.1% and flow stress σ=71.2 MPa at about 865 ℃ and =1.5×10-4 s-1,and could form deep box-shaped pieces with good quality.
中图分类号 TG146.2
所属栏目
基金项目 国防预研项目
收稿日期 2007/7/31
修改稿日期 2007/11/10
网络出版日期
作者单位点击查看
备注陈伟(1980-),男,河南开封人,硕士研究生.
引用该论文: CHEN Wei,CHEN Ming-he,WANG Hui. Superplastic Forming Technology of Box-shaped Piece of High-temperature Titanium Alloy BTi6431S[J]. Materials for mechancial engineering, 2008, 32(6): 40～43
陈伟,陈明和,王辉. BTi6431S高温钛合金盒形件超塑性成型工艺[J]. 机械工程材料, 2008, 32(6): 40～43
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】蔡建明,李臻熙,马济民,等.航空发动机用600 ℃高温钛合金的研究与发展[J].材料导报,2005,19(1):50-53.
【2】曾立英,赵永庆,李丹柯,等.超塑性钛合金的研究进展[J].金属热处理,2005,30(5):28-32.
【3】Ding R,Guo Z X.Microstructural evolution of a Ti6Al4V alloy during phase processing:Experimental and simulation investigate[J].Material Science and Engineering A,2003,365(2):172-179.
【4】陈明和,韩秉强,林兆荣.TC4钛板超塑性成型后的力学性能的研究[J].热加工工艺,1999,5(2):14-16.
【5】张立文,陈磊,王富岗.板材超塑性拉延过程的数值[J].模拟金属成型工艺,2002,20(1):29-31.
【6】张晓华,邱晓刚,卢国清,等.应变速率敏感指数(m值)测试方法探讨[J].钢铁钒钛,2001,22(1):63-68.
【7】陈火红.Marc有限元实例分析教程[M].北京:机械工业出版社,2002.
【8】张凯锋,吴为.超塑成型/扩散连接过程的三维有限元模拟[J].固体力学学报,2000,21(3):267-270.
【9】刘英,李元元,张维平,等.挤压态ZE10镁合金的超塑性研究[J].机械工程材料,2005,29(10):17-19.
【10】顾家琳,孙新军,白秉哲.旋锻制备超细晶双相钛合金及其超塑性[J].金属学报,2002,38(5):378-381.
【2】曾立英,赵永庆,李丹柯,等.超塑性钛合金的研究进展[J].金属热处理,2005,30(5):28-32.
【3】Ding R,Guo Z X.Microstructural evolution of a Ti6Al4V alloy during phase processing:Experimental and simulation investigate[J].Material Science and Engineering A,2003,365(2):172-179.
【4】陈明和,韩秉强,林兆荣.TC4钛板超塑性成型后的力学性能的研究[J].热加工工艺,1999,5(2):14-16.
【5】张立文,陈磊,王富岗.板材超塑性拉延过程的数值[J].模拟金属成型工艺,2002,20(1):29-31.
【6】张晓华,邱晓刚,卢国清,等.应变速率敏感指数(m值)测试方法探讨[J].钢铁钒钛,2001,22(1):63-68.
【7】陈火红.Marc有限元实例分析教程[M].北京:机械工业出版社,2002.
【8】张凯锋,吴为.超塑成型/扩散连接过程的三维有限元模拟[J].固体力学学报,2000,21(3):267-270.
【9】刘英,李元元,张维平,等.挤压态ZE10镁合金的超塑性研究[J].机械工程材料,2005,29(10):17-19.
【10】顾家琳,孙新军,白秉哲.旋锻制备超细晶双相钛合金及其超塑性[J].金属学报,2002,38(5):378-381.
相关信息