35CrMo钢带泵轴断裂原因分析

35CrMo钢带泵轴断裂原因分析

Failure Analysis of 35CrMo Shaft Driving Pump

杨力

王滨

摘要

35CrMo钢带泵轴在使用约40 h后发生断裂,通过宏观断口形貌观察、力学性能试验和金相检验及受力分析等方法对带泵轴断裂原因进行了失效分析.结果表明：带泵轴由于热处理不当造成其疲劳强度降低,服役后发生旋转弯曲疲劳断裂失效.

标签 35CrMo钢

轴

疲劳断裂

失效分析

35CrMo steel

shaft

fatigue fracture

failure analysis

Abstract

Means of macro-analysis,mechanical property test,metallographic analysis and stress analysis were employed to analyze the cracking reason of 35CrMo shaft driving pump which broke after 40 hours using.The results indicated that fatigue strength of the shaft reduced because of the improper heat treating,which led to the rotary bending fatigue fracture of the shaft during service process.

中图分类号 TG162.71

所属栏目

基金项目

收稿日期 2007/8/20

修改稿日期 2008/4/3

网络出版日期

作者单位点击查看

备注杨力(1966-),女,吉林白城人,高级工程师.

引用该论文: YANG Li,WANG Bin. Failure Analysis of 35CrMo Shaft Driving Pump[J]. Materials for mechancial engineering, 2008, 32(6): 78～81
杨力,王滨. 35CrMo钢带泵轴断裂原因分析[J]. 机械工程材料, 2008, 32(6): 78～81

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】机械工业理化检验人员技术培训和资格鉴定委员会.力学性能试验[M].上海:上海科学普及出版社,2003.

【2】机械工程材料性能数据手册编委员.机械工程材料性能数据手册[M].北京:机械工业出版社,1994.

相关信息

	标题	相关频次
	脱硫氧化风机轴断裂原因分析	6
	700 mm轧机轧辊断裂失效分析	4
	采煤机摇臂惰轮断裂失效分析	4
	柴油机球铁曲轴断裂失效分析	4
	柴油机用高强度螺栓断裂失效分析	4
	船用柴油机活塞连接螺栓断裂失效分析	4
	船用柴油机曲轴的断裂原因	4
	大功率风力发电机增速齿轮断裂原因分析	4
	大型柴油机曲轴断裂失效分析	4
	大型发电机转子开裂原因初步分析	4
	风能发电机组结构件的失效分析与预防(待续) 第1讲螺栓的失效分析与预防	4
	高压油泵出油阀紧座断裂失效分析	4
	活塞销失效原因分析	4
	空中积放式推杆悬挂牵引链节断裂失效原因分析	4
	某电厂水冷壁管断裂失效分析	4
	某油田钻铤断裂失效原因分析	4
	纳米压痕技术表征Al₂O₃/3%TiO₂爆炸喷涂涂层的各向异性	4
	纳米压痕试验标准块均匀性的检验	4
	氢气压缩机活塞杆断裂失效分析	4
	沙滩车倒车档轴断裂分析	4
	石油钻铤断裂原因分析	4
	特种设备用钢丝绳断裂的原因	4
	吐丝机螺栓断裂的失效分析	4
	稀土永磁材料NdFeN三种粒度分析方法的比较	4
	TA2受电弓角断裂失效分析	3
	齿轮的失效分析	3
	吊装过程中吊具断裂失效分析	3
	(NH₄)₂SO₄管线开裂失效的原因	2
	0Cr16Ni6热轧退火钢螺纹定位销断裂原因	2
	0Cr17Ni7Al钢制受电弓扭簧断裂原因分析	2