U75V钢的连续冷却相变行为
Continuous Cooling Transformation Behaviour of U75V Steel
摘 要
利用膨胀法结合金相分析在热模拟试验机上测定了U75V钢不同冷却速率下的连续冷却转变膨胀曲线,获得了该钢的连续冷却转变曲线(CCT曲线);研究了冷却速率对钢组织及硬度的影响.结果表明:当冷速小于10 ℃·s-1时,转变产物主要以珠光体为主;当冷速增大到10 ℃·s-1时,得到屈氏体组织和马氏体组织;当冷速增大到10 ℃·s-1以上时,得到马氏体组织;试验钢的硬度随冷却速率的增加而增大.
热模拟
膨胀法
连续冷却转变曲线
U75V steel
thermal simulation
dilatometric test
continuous cooling transformation curve
Abstract
By dilatometric test,microstructure analysis and hardness measurement,the expansion curves of continuous cooling transformation at different cooling rates were determined for U75V rail steel using a hot simulation testing machine,and the continuous cooling transformation curve was obtained.The influence of cooling rate on microstructure and hardness was studied.The results show that the product of austenitie transformation was pearlite when the cooling rate was lower than 10 ℃·s-1.Troostite and martensite were obtained at the cooling rate of 10 ℃·s-1.Only martensite was got if the cooling rate was in the range of 10-50 ℃·s-1.The hardness of the steel increased with the increase of cooling rate.
中图分类号 TB302.3
所属栏目 试验研究
基金项目 武汉市科技计划资助项目(20061002085)
收稿日期 2007/8/24
修改稿日期 2007/10/19
网络出版日期
作者单位点击查看
备注任安超(1976-),男,河南新乡人,工程师,硕士研究生.
引用该论文: REN An-chao,JI Yu,ZHAO Long-qi,SONG Xin-li,SHEN Dong-dong,YUAN Ze-xi. Continuous Cooling Transformation Behaviour of U75V Steel[J]. Materials for mechancial engineering, 2008, 32(7): 15～17
任安超,吉玉,赵隆崎,宋新丽,沈冬冬,袁泽喜. U75V钢的连续冷却相变行为[J]. 机械工程材料, 2008, 32(7): 15～17
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】周镇国.热处理钢轨的组织参数对性能的影响[J].国外金属热处理,1999(3):13-16.
【2】徐权,梅海东,俞梦文,等.钒在钢轨钢中的作用研究[J].钢铁,2001,36(6):44-47.
【3】周跃清,杨来顺.钢轨的材质性能及相关工艺[M].北京:中国铁道出版社,2005.
【4】刘丰收,张银花.基于焊接的UIC900A及U75V钢轨钢连续冷却特性[J].中国铁道科学,2005,26(6):63-68.
【2】徐权,梅海东,俞梦文,等.钒在钢轨钢中的作用研究[J].钢铁,2001,36(6):44-47.
【3】周跃清,杨来顺.钢轨的材质性能及相关工艺[M].北京:中国铁道出版社,2005.
【4】刘丰收,张银花.基于焊接的UIC900A及U75V钢轨钢连续冷却特性[J].中国铁道科学,2005,26(6):63-68.
相关信息