强磁场对Sn-4Cu合金凝固过程中Cu6Sn5相的影响
Effects of High Magnetic Field on Cu6Sn5 Phase of Sn-4Cu Alloy
摘 要
为了研究强磁场对Sn-4Cu合金凝固过程中Cu6Sn5相的影响,对有无强磁场情况下合金的凝固组织进行了对比,通过X射线衍射对晶粒取向进行了分析.结果表明:在磁场作用下的凝固过程中,Cu6Sn5晶体长度增加,有沿磁场方向排列取向的趋势;试样上、底部的Cu6Sn5相形貌存在很大的差异,铜元素的分布变化显著,反映了强磁场对热对流的抑制作用;强磁场对Sn-4Cu合金中各相的影响以及对Cu6Sn5晶体取向的影响比较小.
强磁场
凝固
Cu6Sn5
Sn-4Cu alloy
high magnetic field
solidification
Cu6Sn5
Abstract
A comparison between the solidification structure of Sn-4Cu alloy with and without high magnetic field had been done to investigate the influence of magnetic field on the solidification.The results show that the Cu6Sn5 crystals had grown and aligned along the magnetic field direction.The shape of Cu6Sn5 crystals at the top was different from that at the bottom in the alloy.The Cu element distribution changed from the top to the bottom remarkably.This phenomenon indicates that the high magnetic field restrains heat convection.From the XRD analysis results,it can be found that high magnetic field has slight effect on the Cu6Sn5 crystals orientations.
中图分类号 TG156
所属栏目 试验研究
基金项目 国家自然科学基金资助项目(50471068);“十一五”国家科技支撑计划资助项目(2006BAE03B02-2);国家自然科学基金广东省联合基金重点资助项目(V0734008)
收稿日期 2007/10/17
修改稿日期 2008/5/13
网络出版日期
作者单位点击查看
备注程从前(1982-),男,重庆人,博士研究生.
引用该论文: CHENG Cong-qian,ZHAO Jie,YANG Peng. Effects of High Magnetic Field on Cu6Sn5 Phase of Sn-4Cu Alloy[J]. Materials for mechancial engineering, 2008, 32(10): 27～30
程从前,赵杰,杨朋. 强磁场对Sn-4Cu合金凝固过程中Cu6Sn5相的影响[J]. 机械工程材料, 2008, 32(10): 27～30
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】彭涛,辜承林.强磁场发展动态与趋势[J].前沿进展,2004,33(8):570-573.
【2】李喜,王晖,任忠明,等.稳恒强磁场技术的发展及其在材料科学中的应用[J].材料导报,2002,16(10):25-27.
【3】马衍伟,肖立业,严陆光.强磁场条件下材料制备及其研究进展[J].科学通报,2006,51(24):2825-2829.
【4】陈东风,曹志强,杨淼,等.强磁场在材料科学中的应用现状及理论分析[J].钢铁研究,1997,35(3):58-62.
【5】王强,王春江,王恩刚,等.强磁场对不同磁化率非磁性金属凝固组织的影响[J].金属学报,2005,41(2):128-132.
【6】Li X,Ren Z M,Faurtrelly Y,et al.The alignment,aggregation and magnetization behaviors in MnBi-Bi composites solidified under a high magnetic field[J].Intermetallics,2007,15(7):845-855.
【7】Yasuda H,Nakahira A,Ohnaka I,et al.Formation of crystallographically aligned grains during coarsening in a magnetic field[J].Materials Transactions,2003,44(12):2555-2562.
【8】宛德福,罗世华.磁性物理[M].北京:电子工业出版社,1987.
【9】Yasuda H,Fujimoto S,Hayashi Y,et al.Proceeding of the 4th International Symposium on Electro-magnetic Processing of Materials[C]//Lyon:CNRS,COST P6,EDF,ATS,UIE,EFGP,SF2M and FEMS,2003:474.
【2】李喜,王晖,任忠明,等.稳恒强磁场技术的发展及其在材料科学中的应用[J].材料导报,2002,16(10):25-27.
【3】马衍伟,肖立业,严陆光.强磁场条件下材料制备及其研究进展[J].科学通报,2006,51(24):2825-2829.
【4】陈东风,曹志强,杨淼,等.强磁场在材料科学中的应用现状及理论分析[J].钢铁研究,1997,35(3):58-62.
【5】王强,王春江,王恩刚,等.强磁场对不同磁化率非磁性金属凝固组织的影响[J].金属学报,2005,41(2):128-132.
【6】Li X,Ren Z M,Faurtrelly Y,et al.The alignment,aggregation and magnetization behaviors in MnBi-Bi composites solidified under a high magnetic field[J].Intermetallics,2007,15(7):845-855.
【7】Yasuda H,Nakahira A,Ohnaka I,et al.Formation of crystallographically aligned grains during coarsening in a magnetic field[J].Materials Transactions,2003,44(12):2555-2562.
【8】宛德福,罗世华.磁性物理[M].北京:电子工业出版社,1987.
【9】Yasuda H,Fujimoto S,Hayashi Y,et al.Proceeding of the 4th International Symposium on Electro-magnetic Processing of Materials[C]//Lyon:CNRS,COST P6,EDF,ATS,UIE,EFGP,SF2M and FEMS,2003:474.
相关信息