减速机齿轮断裂失效分析
Fracture Analysis of Gears of a Speed Reducer
摘 要
某搅拌器减速机齿轮轴和齿轮在服役1 a后发生了断裂失效;通过显微组织分析、断口分析、力学性能测试等方法对其失效原因进行了分析.结果表明:轴和齿轮的断裂均为疲劳断裂,轴的断裂先于齿轮的断裂;搅拌轴装配不当造成的过载是导致轴首先产生疲劳断裂的原因.
齿轮
疲劳失效
装配
过载
shaft
gear
fatigue failure
assemble
overload
Abstract
The failure of a shaft and gears of a speed reducer after serving for a year was investigated by means of microstructure observetion,scanning electron microscopy (SEM),hardness test and tension test.The results showed that the failure of the shaft and gears was fatigue fracture and the fracture of the shaft occurred firstly.The fatigue crack initiated from an overload.Incorrect assemble was responsible for the overload of the shaft.
中图分类号 TB303
所属栏目 失效分析
基金项目
收稿日期 2007/11/5
修改稿日期 2008/8/8
网络出版日期
作者单位点击查看
备注尤兆宏(1965-),男,上海人,高级工程师.
引用该论文: YOU Zhao-hong. Fracture Analysis of Gears of a Speed Reducer[J]. Materials for mechancial engineering, 2008, 32(12): 82～84
尤兆宏. 减速机齿轮断裂失效分析[J]. 机械工程材料, 2008, 32(12): 82～84
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】美国金属学会.金属手册,失效分析与预防[M].北京:机械工业出版社,1986:141-143.
【2】孙志礼.机械设计[M].沈阳:东北大学出版社,2000.
【3】金蔚静.发电机转轴断裂失效分析[J].理化检验-物理分册,2003,39(1):50-52.
【2】孙志礼.机械设计[M].沈阳:东北大学出版社,2000.
【3】金蔚静.发电机转轴断裂失效分析[J].理化检验-物理分册,2003,39(1):50-52.
相关信息