Fe24Mn0.5C形变孪晶诱发塑性钢的显微组织和力学性能
Microstructure and Mechanical Properties of Fe24Mn0.5C TWIP Steel
摘 要
采用光学显微镜、X射线衍射仪和电子万能试验机等研究了Fe24Mn0.5C形变孪晶诱发塑性钢的组织和力学性能.结果表明：该钢在室温下为单一的奥氏体组织,拉伸时产生形变孪晶诱发塑性效应,开始产生形变孪晶,并且随着应变量的增加形变孪晶逐渐增加;随着拉伸速度减小,该钢的均匀伸长率呈轻微上升趋势,但屈服强度、抗拉强度和断后伸长率明显升高;与高强度应变诱发塑性590钢相比,该钢具有较高的能量吸收值.
显微组织
力学性能
TWIP steel
microstructure
mechanical property
Abstract
The microstructure and mechanical properties of the Fe24Mn0.5C twinning induced plasticity(TWIP) steel were investigated using optical microscope,XRD and universal tensile testing machine.The results show that the microstructure of the tested steel was austenite at room temperature.Deformation twin appeared during tensile test and increased with increasing strain.When the tensile speed decreased the uniform elongation increased lightly,however the yield strength ,tensile strength and elongation after fracture increased obviously.Compared with TRIP590 high strength steel,the energy absorption of the test steel was higher.
中图分类号 TG142.25
所属栏目 试验研究
基金项目 国家自然科学基金资助项目(50671061)
收稿日期 2008/3/31
修改稿日期 2009/2/26
网络出版日期
作者单位点击查看
备注周小芬(1983-),女,江苏常州人,硕士研究生.
引用该论文: ZHOU Xiao-fen,FU Ren-yu,LI Lin. Microstructure and Mechanical Properties of Fe24Mn0.5C TWIP Steel[J]. Materials for mechancial engineering, 2009, 33(5): 22～25
周小芬,符仁钰,李麟. Fe24Mn0.5C形变孪晶诱发塑性钢的显微组织和力学性能[J]. 机械工程材料, 2009, 33(5): 22～25
被引情况:
【1】刘龙龙,赵玲燕,王吉良,轩建伟,朱定一, "非金属夹杂物对高碳含铜TWIP钢拉伸性能的影响",机械工程材料 39, 59-64(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】苏凯,余际星,徐建兵.新型汽车用高强度钢的应用现状和发展趋势[J].钢铁钒钛,2006,27(4):53-56.
【2】MI Zheng-li,TANG Di,YAN Ling.High-strength and high plasticity TWIP steel for modern vehicle[J].Material Science and Technology,2005,21(4):451-454.
【3】FROMMEYER G.Super-ductile and high-strength ,manganese-TRIP/TWIP steels for high energy absorption purpose[J].ISIJ International,2003,43:438-441.
【4】GRASSEL O,KRUGER L,FROMMEYER G.High strenth Fe-Mn-(Al,Si)TRIP/TWIP steels development-properties-application[J].IntJ Plasticity,2000,16:1391-1396.
【5】代永娟,米振莉,唐荻.Fe-Mn-C系TWIP钢的组织和性能[J].上海金属,2007,29(5):132-136.
【6】熊荣刚.TWIP钢不同应变速率下应变行为研究[D].上海:上海大学,2008.
【7】陈卡尔.汽车用高强度钢的高应变速率[J].鞍钢技术,2005(1):50-53.
【8】唐狄.相变诱导塑性钢的研究现状与发展方向[J].鞍钢技术,2008(2):2-5.
【2】MI Zheng-li,TANG Di,YAN Ling.High-strength and high plasticity TWIP steel for modern vehicle[J].Material Science and Technology,2005,21(4):451-454.
【3】FROMMEYER G.Super-ductile and high-strength ,manganese-TRIP/TWIP steels for high energy absorption purpose[J].ISIJ International,2003,43:438-441.
【4】GRASSEL O,KRUGER L,FROMMEYER G.High strenth Fe-Mn-(Al,Si)TRIP/TWIP steels development-properties-application[J].IntJ Plasticity,2000,16:1391-1396.
【5】代永娟,米振莉,唐荻.Fe-Mn-C系TWIP钢的组织和性能[J].上海金属,2007,29(5):132-136.
【6】熊荣刚.TWIP钢不同应变速率下应变行为研究[D].上海:上海大学,2008.
【7】陈卡尔.汽车用高强度钢的高应变速率[J].鞍钢技术,2005(1):50-53.
【8】唐狄.相变诱导塑性钢的研究现状与发展方向[J].鞍钢技术,2008(2):2-5.
相关信息