激光辐照参数对自蔓延合成铝-钛-硼中间合金组织和性能的影响
Influence of Laser Parameters on Microstructure and Property of Al-Ti-B Master Alloy Prepared by Laser-induced SHS
摘 要
采用激光引燃自蔓延技术合成铝-钛-硼中间合金,利用此中间合金可对ZL108铝合金组织进行细化,研究了激光辐照参数对中间合金和铝合金显微组织的影响.结果表明:通过对激光器工作参数的调整,可制备出具有TiAl3和TiB2颗粒含量适中、弥散分布的中间合金;在本试验条件下,激光功率1 200 W、照射1.0 s时,生成粒径约为1 μm、弥散分布的TiB2,长度约10 μm、均匀分布的长条状TiAl3,此时中间合金的细化效果最佳,铝晶粒平均尺寸为55 μm.
自蔓延合成
晶粒细化
铝-钛-硼中间合金
laser
SHS
refinement grain
Al-Ti-B master alloy
Abstract
Self-propagating high-temperature synthesis(SHS) was ignited by the laser to synthesize Al-Ti-B master alloy,and the master alloy was used to refine ZL108 Al alloy.The influences of laser parameters on microstructure of Al-Ti-B master alloy and ZL108 alloy were analyzed.The results show that master alloy with proper TiAl3 and TiB2 particles which distributed dispersively by laser parameters adjusting.When the laser illumination time was 1.0 s and the power was 1 200 W,the distribution of TiB2 was dispersing,and the average size of TiB2 was about 1 μm.The distribution of strip-shaped TiAl3 was uniform and the length was about 10 μm;the microstructure of the master alloy was fine and the refinement effect was the best with the average Al grain size of 55 μm.
中图分类号 TG146.2
所属栏目 试验研究
基金项目 国家自然科学基金资助项目(50704009);辽宁省博士启动基金资助项目(20031081)
收稿日期 2008/6/12
修改稿日期 2009/6/15
网络出版日期
作者单位点击查看
备注李勇(1983-),男,黑龙江绥化人,助理工程师.
引用该论文: LI Yong,ZHUANG Hong-yu,PAN Xue-min. Influence of Laser Parameters on Microstructure and Property of Al-Ti-B Master Alloy Prepared by Laser-induced SHS[J]. Materials for mechancial engineering, 2009, 33(9): 13～16
李勇,庄洪宇,潘学民. 激光辐照参数对自蔓延合成铝-钛-硼中间合金组织和性能的影响[J]. 机械工程材料, 2009, 33(9): 13～16
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李升.活塞用新型过共晶铝硅合金的研究[J].中国铸造装备与技术,1997(2):19-21.
【2】LIMMANEEVICHITR C,EIDHED W.Fading Mechanism of grain refinement of Al-Si alloy with Al-Ti-B grain refiners[J].Materials Science and Engineering A,2003,349:197-206.
【3】RAO A A,MURTY B S,CHAKRABORTY M.Role of zirconium and impurtities in grain refinement of aluminum with Al-Ti-B[J].Mater Sci Tiechnol,1997,13(9):769-777.
【4】VENKATESWARLU K,CHAKRABORTY M,MURTY B S.Influence of thermo-mechanical processing of Al-5Ti-1B master alloy on its grain refining efficiency [J].Materials Science and Engineering,2004,A364:75-83.
【5】张虎,高文理,张二林,等.Al-54Ti-xB合金中TiB2的形貌演变及生长机理[J].金属学报,2002,38(7):699-702.
【6】于亚鑫,邱竹贤.Ti-B及其Al-Ti-B中间合金的研制[J].轻金属,1988(5):30-33.
【7】LI Pei-jie,KANDALOVA E G,NIKITIN V I,et al.Effect of fluxes on structure formation of SHS Al-Ti-B grain refiner[J].Materials Letters,2003,57:3694-3698.
【8】JONES G P,PEARSON J.Factors affecting the grain refinement of aluminum using titanium and boron additives [J].Metall Trans B,1976,7B:223-234.
【9】张作贵,刘相法,边秀房,等.Al-Ti-B中间合金中的化合物形态[J].中国有色金属学报,1999,9(4):736-739.
【10】WANG Yan,ZHANG Zhong-hua,WANG Wei-min,et al.Microstructural evolution and microhardness of a meltspun Al-5Ti-1B alloy during annealing[J].Materials Science and Engineering A,2004,350:17-24.
【2】LIMMANEEVICHITR C,EIDHED W.Fading Mechanism of grain refinement of Al-Si alloy with Al-Ti-B grain refiners[J].Materials Science and Engineering A,2003,349:197-206.
【3】RAO A A,MURTY B S,CHAKRABORTY M.Role of zirconium and impurtities in grain refinement of aluminum with Al-Ti-B[J].Mater Sci Tiechnol,1997,13(9):769-777.
【4】VENKATESWARLU K,CHAKRABORTY M,MURTY B S.Influence of thermo-mechanical processing of Al-5Ti-1B master alloy on its grain refining efficiency [J].Materials Science and Engineering,2004,A364:75-83.
【5】张虎,高文理,张二林,等.Al-54Ti-xB合金中TiB2的形貌演变及生长机理[J].金属学报,2002,38(7):699-702.
【6】于亚鑫,邱竹贤.Ti-B及其Al-Ti-B中间合金的研制[J].轻金属,1988(5):30-33.
【7】LI Pei-jie,KANDALOVA E G,NIKITIN V I,et al.Effect of fluxes on structure formation of SHS Al-Ti-B grain refiner[J].Materials Letters,2003,57:3694-3698.
【8】JONES G P,PEARSON J.Factors affecting the grain refinement of aluminum using titanium and boron additives [J].Metall Trans B,1976,7B:223-234.
【9】张作贵,刘相法,边秀房,等.Al-Ti-B中间合金中的化合物形态[J].中国有色金属学报,1999,9(4):736-739.
【10】WANG Yan,ZHANG Zhong-hua,WANG Wei-min,et al.Microstructural evolution and microhardness of a meltspun Al-5Ti-1B alloy during annealing[J].Materials Science and Engineering A,2004,350:17-24.
相关信息