60Si2Mn弹簧扁钢崩料断裂原因分析
Reason Analysis for Avalanche Fracture of 60Si2Mn Spring Flat Steel
摘 要
60Si2Mn弹簧扁钢在下料过程中发生崩断现象,采用化学成分分析、显微组织分析、力学性能试验等方法对弹簧扁钢的断裂原因进行了分析.结果表明:弹簧扁钢崩料断裂性质为解理断裂;材料原始组织中存在超标的非金属夹杂物是导致弹簧扁钢发生崩断的主要原因,钢中的非金属夹杂物在外力作用下形成裂纹源,随后在下料过程中受力导致裂纹扩展而发生了崩料断裂.
断裂
解理断裂
非金属夹杂物
60Si2Mn spring flat steel
fracture
cleavage fracture
non-metallic inclusion
Abstract
During the cutting process,60Si2Mn spring flat steel had the avalanche problem.A study was conducted to investigate the 60Si2Mn spring flat steel fracture reason by means of chemical analysis,microstructure testing and mechanical properties testing,etc.The results show that the property of fracture was cleavage fracture.In the spring flat steel,there were a large number of non-metallic inclusions caused the avalanche problem.Under the external force,non-metallic inclusions were the source of cracks which resulted in the crack propagation and led to avalanche fracture finally.
中图分类号 TG142.75
所属栏目 失效分析
基金项目
收稿日期 2008/11/14
修改稿日期 2009/7/31
网络出版日期
作者单位点击查看
备注万正东(1980-),男,江苏江都人,硕士研究生.
引用该论文: WAN Zheng-dong,PENG Wen-yi,YANG Xiang-jie,TANG Xiao-jun,CHEN Ming. Reason Analysis for Avalanche Fracture of 60Si2Mn Spring Flat Steel[J]. Materials for mechancial engineering, 2009, 33(12): 94～97
万正东,彭文屹,杨湘杰,唐小军,陈明. 60Si2Mn弹簧扁钢崩料断裂原因分析[J]. 机械工程材料, 2009, 33(12): 94～97
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张先鸣.弹簧钢高强度化的现状及发展趋势[J].现代零部件,2006(7):64-65.
【2】崔忠圻.金属学与热处理[M].北京:机械工业出版社,2000.
【3】李英,孟羽,聂爱诚,等.连铸连轧弹簧扁钢侧面裂纹的原因分析[J].江苏冶金,2006,34(5):51-55.
【2】崔忠圻.金属学与热处理[M].北京:机械工业出版社,2000.
【3】李英,孟羽,聂爱诚,等.连铸连轧弹簧扁钢侧面裂纹的原因分析[J].江苏冶金,2006,34(5):51-55.
相关信息