Effect of Li,V Dope on Sintering Temperature and Dielectric Properties of Bi2(Zn1/3Nb2/3)2O7 Ceramics
摘 要
采用固相反应法制备出了(Bi1.975Li0.025)(Zn2/3Nb4/3-xVx)O7陶瓷,研究了锂、钒掺杂对于Bi2(Zn1/3Nb2/3)2O7(BZN)陶瓷烧结温度、相结构和介电性能的影响.结果表明:锂、钒掺杂能显著降低BZN陶瓷的烧结温度,可由1 000 ℃降至860 ℃;当掺杂量x≤0.05时,陶瓷相结构保持单一的单斜焦绿石相,介电损耗出现明显的弛豫现象;当x为0.005,0.01,0.02和0.05时,陶瓷的介电弛豫峰值温度分别为125,120,112,100 ℃,介电弛豫激活能的减小使弛豫温区向低温方向移动.
Abstract
(Bi1.975Li0.025)(Zn2/3Nb4/3-xVx)O7(BLZNV) ceramics were prepared by solid phase reaction.The effect of(Li,V) dope on sintering temperature,phase structure and dielectric properties of Bi2(Zn1/3Nb2/3)2O7(BZN) ceramics was investigated.The results show that(Li,V) doping could decrease the sintering temperature of the BZN ceramic remarkably from 1 000 ℃ to 860 ℃.The ceramics had single monoclinal pyrochlore phase when x≤005.Relaxation appeared during dielectric loss.When x were 0.005,0.01,0.02 and 0.05,the peak temperatures of(Li,V) doped samples were 125,120,112 and 100 ℃,respectively.A shift of the relaxation peak to low temperature was caused by activation energy decreasing.
中图分类号 TM28
所属栏目 试验研究
基金项目 四川省教育厅科技基金资助项目(2006C025)
收稿日期 2009/2/20
修改稿日期 2009/8/2
网络出版日期
作者单位点击查看
备注张东(1981-),男,四川彭山人,硕士研究生.
引用该论文: ZHANG Dong,DING Shi-hua,SONG Tian-xiu,YANG Xiu-ling. Effect of Li,V Dope on Sintering Temperature and Dielectric Properties of Bi2(Zn1/3Nb2/3)2O7 Ceramics[J]. Materials for mechancial engineering, 2010, 34(2): 21~24
张东,丁士华,宋天秀,杨秀玲. 锂、钒掺杂对Bi2(Zn1/3Nb2/3)2O7陶瓷烧结温度和介电性能的影响[J]. 机械工程材料, 2010, 34(2): 21~24
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】SHEN B,ZHAI J W,YAO X.Dielectric relaxation and tunability of Bi2O3-ZnO-CaO-Ta2O5 ceramics [J].Appl Phys Lett,2005,86(7):1-3.
【2】沈波,刘艳平,姚熹.(Bi2-yCay)(Zn1/3Ta2/3)2O7陶瓷的介电弛豫和介电性能[J].硅酸盐学报,2006,34(2):237-241.
【3】YAN M F,LING H C,RHODES W W.Low-firing,temperature stable dielectric compositions based on bismuth nickel zinc niobates[J].J Am Ceram Soc,1990,73(4):1106-1109.
【4】VALANT M,DAVIES P K.Crystal chemistry and dielectric properties of chemically substituted(Bi1.5Zn1.0Nb1.5)O7 and Bi2(Zn1/3Nb2/3)2O7 pyrochlores[J].J Am Ceram Soc,2000,83(1):147-156.
【5】JUAN C N,MICHAEL T L,CLIVE A Rl.Dielectric relaxation in Bi2O3-ZnO-Nb2O5 cubic pyrochlore[J].Journal of Applied Physics,2001,89(8):4512-4516.
【6】YEE K A,HAN K R,KIM H T.The effect of V2O5 on sintability and physical properties of Bi2O3-NiO-Nb2O5 and Bi2O3-ZnO-Nb2O5 temperature temperature-stable dielectrics[J].J Mater Sci,1999,34(19):4699-4704.
【7】周焕福,黄金亮,王茹玉,等.BiVO4掺杂对(Bi1.5Zn0.5)(Zn0.5Nb1.5)O7陶瓷介电性能的影响[J].硅酸盐学报,2005,33(12):1453-1456.
【8】孙目珍.电介质物理基础[D].广州:华南理工大学,2005:115-122.
【9】JONSCHER A K.Dielectric relaxation in solids[M].London:Chlesea Dielectrics,1983:326-335.
【10】SMYTH D M.The defect chemistry of metal oxides[M].Oxford:Oxford University Press,2000:75-85.
【11】彭邓山.中介电常数Bi基微波介质材料的研究[D].上海:同济大学,2004:35-38.
【12】CHEN A,YU Z,YOUN H J,et al.Dielectric properties of Bi2O3-ZnO-Ta2O5 pyrochlore and zirconolite structure ceramics[J].Appl Phys Lett,2003,82(21):3734-3736.
【2】沈波,刘艳平,姚熹.(Bi2-yCay)(Zn1/3Ta2/3)2O7陶瓷的介电弛豫和介电性能[J].硅酸盐学报,2006,34(2):237-241.
【3】YAN M F,LING H C,RHODES W W.Low-firing,temperature stable dielectric compositions based on bismuth nickel zinc niobates[J].J Am Ceram Soc,1990,73(4):1106-1109.
【4】VALANT M,DAVIES P K.Crystal chemistry and dielectric properties of chemically substituted(Bi1.5Zn1.0Nb1.5)O7 and Bi2(Zn1/3Nb2/3)2O7 pyrochlores[J].J Am Ceram Soc,2000,83(1):147-156.
【5】JUAN C N,MICHAEL T L,CLIVE A Rl.Dielectric relaxation in Bi2O3-ZnO-Nb2O5 cubic pyrochlore[J].Journal of Applied Physics,2001,89(8):4512-4516.
【6】YEE K A,HAN K R,KIM H T.The effect of V2O5 on sintability and physical properties of Bi2O3-NiO-Nb2O5 and Bi2O3-ZnO-Nb2O5 temperature temperature-stable dielectrics[J].J Mater Sci,1999,34(19):4699-4704.
【7】周焕福,黄金亮,王茹玉,等.BiVO4掺杂对(Bi1.5Zn0.5)(Zn0.5Nb1.5)O7陶瓷介电性能的影响[J].硅酸盐学报,2005,33(12):1453-1456.
【8】孙目珍.电介质物理基础[D].广州:华南理工大学,2005:115-122.
【9】JONSCHER A K.Dielectric relaxation in solids[M].London:Chlesea Dielectrics,1983:326-335.
【10】SMYTH D M.The defect chemistry of metal oxides[M].Oxford:Oxford University Press,2000:75-85.
【11】彭邓山.中介电常数Bi基微波介质材料的研究[D].上海:同济大学,2004:35-38.
【12】CHEN A,YU Z,YOUN H J,et al.Dielectric properties of Bi2O3-ZnO-Ta2O5 pyrochlore and zirconolite structure ceramics[J].Appl Phys Lett,2003,82(21):3734-3736.
相关信息