Wear Resistance of High Speed Steel with DLC Surface Coating
摘 要
在高速钢基体上分别进行了制备类金刚石(DLC)膜和浸硫氮化两种表面处理,并以铸铁为对偶件,用MM200磨损试验机比较了经两种不同表面处理高速钢的耐磨性能,用扫描电子显微镜观察了磨痕形貌并分析了磨损机理.结果表明:在转速200 r·min-1、载荷50 N的条件下,不论在油润滑状态还是在干摩擦状态,具有DLC膜高速钢的耐磨性能明显比浸硫氮化处理的好.
Abstract
Two different surface treatments of diamond-like carbon(DLC) film preparation and sulfonitriding surface treatment were carried out on high speed steels.The wear resistance of high speed steels with different surface treatments running against cast iron alloy was investigated by using MM-200 friction and wear tester.The micrographs of the wear track were observed by SEM and the wear mechanism was analyzed.It is revealed that high speed steels with DLC films had better wear resistance compared to that of sulfonitriding surface treatment with the speed of 200 r·min-1 and the load of 50 N,no matter under conditions of oil lubrication or dry friction.
中图分类号 TB43 TH117.1
所属栏目 材料性能及其应用
基金项目
收稿日期 2009/3/13
修改稿日期 2009/9/10
网络出版日期
作者单位点击查看
备注戴兵(1984-),男,江苏东台人,硕士研究生.
引用该论文: DAI Bing,WANG Bo,ZHANG Heng-hua,HUANG Bo,GAO Guo-qiang. Wear Resistance of High Speed Steel with DLC Surface Coating[J]. Materials for mechancial engineering, 2010, 34(4): 51~54
戴兵,王博,张恒华,黄波,高国强. 具有表面类金刚石膜高速钢的耐磨性能[J]. 机械工程材料, 2010, 34(4): 51~54
被引情况:
【1】朱涛,刘政,邓可月,沈俊波,吴强, "交变磁处理参数对W6Mo5Cr4V2高速钢硬度的影响",机械工程材料 39, 52-55(2015)
【2】王博,张恒华, "11Cr17马氏体不锈钢浸硫氮化后的耐磨性能",机械工程材料 35, 12-15(2011)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钱苗根,姚寿山,张少宗.现代表面技术[M].北京:机械工业出版社,2002.
【2】赵文轸.材料表面工程导论[M].西安:西安交通大学出版社,1998.
【3】张红,宋玉悟.硫氮共渗后磨损粘着特性的研究[J].材料科学与工艺,1997,5(1):65-67.
【4】刘家浚.材料磨损原理及其耐磨性[M].北京:清华大学出版社,1993.
【5】祝土富,沈丽如.类金刚石膜的性能、制备与应用[J].真空,2007,44(6):24-29.
【6】ROBERTSON J.Diamond-like amorphous carbon[J].Materials Science and Engineering,2002,37(4/6):129-281.
【7】HAUERT R.An overview on the tribological behavior of diamond-like carbon in technical and medical applications[J].Tribology International,2004,37(11):991-1003.
【8】ERDEMIR A,BINDAL C,FENSKE G R,et al.Characteri-zation of transfer layers forming on surfaces sliding against diamond-like carbon[J].Surface and Coating Technology,1996,86/87(1/3):692-697.
【9】ZHOU Z F,LI K Y,BELLO I,et al.Study of tribological performance of ECR-CVD diamond-like carbon coatings on steel substrates[J].Wear,2005,258(10):1589-1599.
【10】LIU Yan,MELETIS E I.Evidence of graphitization of diamond like carbon films during sliding wear[J].Journal of Materials Science,1997,32(13):3491-3495.
【11】蔡长龙,王季梅,杭凌侠,等.类金刚石薄膜硬度的研究[J].表面技术,2002,31(3):9-11.
【12】张瑞军,马洪涛.掺氮类金刚石薄膜的纳米力学及纳米摩擦特性研究[J].摩擦学学报,2005,25(6):530-534.
【13】曾群锋,董光能,谢友柏,等.高速钢表面镀覆DLC膜的结构及其摩擦特性研究[J].润滑与密封,2007,32(10):25-28.
【2】赵文轸.材料表面工程导论[M].西安:西安交通大学出版社,1998.
【3】张红,宋玉悟.硫氮共渗后磨损粘着特性的研究[J].材料科学与工艺,1997,5(1):65-67.
【4】刘家浚.材料磨损原理及其耐磨性[M].北京:清华大学出版社,1993.
【5】祝土富,沈丽如.类金刚石膜的性能、制备与应用[J].真空,2007,44(6):24-29.
【6】ROBERTSON J.Diamond-like amorphous carbon[J].Materials Science and Engineering,2002,37(4/6):129-281.
【7】HAUERT R.An overview on the tribological behavior of diamond-like carbon in technical and medical applications[J].Tribology International,2004,37(11):991-1003.
【8】ERDEMIR A,BINDAL C,FENSKE G R,et al.Characteri-zation of transfer layers forming on surfaces sliding against diamond-like carbon[J].Surface and Coating Technology,1996,86/87(1/3):692-697.
【9】ZHOU Z F,LI K Y,BELLO I,et al.Study of tribological performance of ECR-CVD diamond-like carbon coatings on steel substrates[J].Wear,2005,258(10):1589-1599.
【10】LIU Yan,MELETIS E I.Evidence of graphitization of diamond like carbon films during sliding wear[J].Journal of Materials Science,1997,32(13):3491-3495.
【11】蔡长龙,王季梅,杭凌侠,等.类金刚石薄膜硬度的研究[J].表面技术,2002,31(3):9-11.
【12】张瑞军,马洪涛.掺氮类金刚石薄膜的纳米力学及纳米摩擦特性研究[J].摩擦学学报,2005,25(6):530-534.
【13】曾群锋,董光能,谢友柏,等.高速钢表面镀覆DLC膜的结构及其摩擦特性研究[J].润滑与密封,2007,32(10):25-28.
相关信息