烟机静叶固定螺栓的失效分析
Failure Analysis of Fixed Bolts in Tobacco Machinery Fixed Blade
摘 要
为查明某烟机静叶固定螺栓的断裂原因,对螺栓的成分、断裂形貌和材料性能等进行了分析.结果表明:螺栓断裂为脆性断裂,螺栓的伸长率、断面收缩率偏低和材料中存在较多的硫元素是螺栓失效的主要原因.建议选择对高温硫化腐蚀不敏感的材料制造螺栓,并优化热加工工艺.
高温合金
失效分析
bolt
high temperature alloy
failure analysis
Abstract
The failure analysis of blades was performed in terms of composition analysis,fracture morphology observing and mechanical tests to find out the fracture reason of bolts in tobacco machinery fixed blade.The results show that the fracture of the bolts was brittle rupture.The relatively low elongation and area reduction of the bolts and the relatively high content of sulfur element in the material were main causes of failure.It is suggested to select materials insensitive to high-temperature sulfidation for preparing the bolts and optimize thermal treatment processing.
中图分类号 TG132
所属栏目 失效分析
基金项目 国家自然科学基金资助项目(50805048);上海市自然科学基金资助项目(08ZR1405700);教育部新教师基金资助项目(200802511008)
收稿日期 2009/4/7
修改稿日期 2009/9/14
网络出版日期
作者单位点击查看
备注王卫泽(1975-),女,黑龙江哈尔滨人,副研究员,博士.
引用该论文: WANG Wei-ze,LIANG Jia-chun,WANG Bo,XUAN Fu-zhen. Failure Analysis of Fixed Bolts in Tobacco Machinery Fixed Blade[J]. Materials for mechancial engineering, 2010, 34(4): 84～86
王卫泽,梁佳春,王博,轩福贞. 烟机静叶固定螺栓的失效分析[J]. 机械工程材料, 2010, 34(4): 84～86
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】严春莲,温娟,刘晓岚,等.吐丝机螺栓断裂的失效分析[J].理化检验-物理分册,2008,44(6):316-318,324.
【2】赵楠,穆海玲,周丽萍,等.35CrMoA钢连杆螺栓断裂失效分析[J].金属热处理,2008,33(9):111-114.
【3】王玉玲,王俊.30CrMnSiA螺栓失效分析[J].机械工程材料,2008,32(5):71-73.
【4】ZHU G,QIU Y,YANG Z.Failure analysis of ruptured bolts in coal gas heater[J].Journal of Fudan University: Natural Science,2008,47(3):391-397.
【5】孙大亮,李玲琴,贺庆华,等.3t装载机发动机地脚螺栓断裂故障排除[J].工程机械,2008,39(11):71-73.
【6】刘昌奎,李运菊,陶春虎,等.紧固螺栓开裂原因分析[J].机械工程材料,2008,32(4):70-73.
【7】LACALLE R,CICERO S,FERRENO D,et al.Failure analysis of a bolt in a scaffolding system[J].Engineering Failure Analysis,2008,15:237-246.
【8】LEE H,CHOI J,LEE B,et al.Failure analysis of stress corrosion cracking in aircraft bolts[J].Engineering Failure Analysis,2007,14:209-217.
【9】《高温合金手册》编写组.高温合金手册[M].北京:冶金工业出版社,1972:191.
【10】翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994:111.
【11】朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995:263.
【2】赵楠,穆海玲,周丽萍,等.35CrMoA钢连杆螺栓断裂失效分析[J].金属热处理,2008,33(9):111-114.
【3】王玉玲,王俊.30CrMnSiA螺栓失效分析[J].机械工程材料,2008,32(5):71-73.
【4】ZHU G,QIU Y,YANG Z.Failure analysis of ruptured bolts in coal gas heater[J].Journal of Fudan University: Natural Science,2008,47(3):391-397.
【5】孙大亮,李玲琴,贺庆华,等.3t装载机发动机地脚螺栓断裂故障排除[J].工程机械,2008,39(11):71-73.
【6】刘昌奎,李运菊,陶春虎,等.紧固螺栓开裂原因分析[J].机械工程材料,2008,32(4):70-73.
【7】LACALLE R,CICERO S,FERRENO D,et al.Failure analysis of a bolt in a scaffolding system[J].Engineering Failure Analysis,2008,15:237-246.
【8】LEE H,CHOI J,LEE B,et al.Failure analysis of stress corrosion cracking in aircraft bolts[J].Engineering Failure Analysis,2007,14:209-217.
【9】《高温合金手册》编写组.高温合金手册[M].北京:冶金工业出版社,1972:191.
【10】翟金坤.金属高温腐蚀[M].北京:北京航空航天大学出版社,1994:111.
【11】朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995:263.
相关信息