粉末冶金法制备镁-硅-锆合金的组织及性能
Microstructure and Properties of Mg-Si-Zr Magnesium Alloy Prepared by Powder Metallurgy
摘 要
采用粉末冶金方法制备了镁-硅-锆合金,并研究了硅含量对合金显微组织和力学性能的影响.结果表明:合金粉在球磨过程中没有发生合金化,锆、硅、镁仍以单质形式存在;合金粉成型烧结后有Mg2Si新相生成,且该相的数量随硅含量的增加而增多;合金的抗弯强度和硬度也随着硅含量的增加而增大,且当硅质量分数为6%时抗弯强度达到132 MPa.
粉末冶金
显微组织
力学性能
Mg-Si-Zr alloy
powder metallurgy
microstructure
mechanical property
Abstract
Mg-Si-Zr alloys were prepared by powder metallurgy.The effect of Si content on microstructure and mechanical properties was investigated.The results indicate that the alloy powders were not mechanically alloyed during the ball milling process,Zr,Si and Mg still existed as elementary substances.The Mg2Si phase was formed after sintering,the amount of the new phase increased with the increase of Si content.The bending strength and hardness were also enhanced with the increase of Si content,and the Mg-6wt%Si-Zr alloy had maximum bending strength of 132 MPa.
中图分类号 TG146.2
所属栏目 新材料 新工艺
基金项目 航空科学联合基金资助项目(2008ZF52058)
收稿日期 2009/4/27
修改稿日期 2009/9/30
网络出版日期
作者单位点击查看
备注杨明(1982-),男,江苏泰州人,硕士研究生.
引用该论文: YANG Ming,LIU Zi-li,LIU Xi-liang,FEI Fei. Microstructure and Properties of Mg-Si-Zr Magnesium Alloy Prepared by Powder Metallurgy[J]. Materials for mechancial engineering, 2010, 34(5): 33～35
杨明,刘子利,刘细良,费飞. 粉末冶金法制备镁-硅-锆合金的组织及性能[J]. 机械工程材料, 2010, 34(5): 33～35
被引情况:
【1】陈泓谕,罗来马,谭晓月,李萍,吴玉程, "纤维增韧钨基复合材料的研究现状",机械工程材料 39, 10-15(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】彭晓东,李玉兰,刘江.轻合金在汽车上的应用[J].机械工程材料,1999,23(2):1-4.
【2】BROWN B.49th annual IMA world magnesium conference[J].Light Metal Age,1992,50(5/6):21-24.
【3】ROBERT B,ARONSON.Materials for the next generation vehicle[J].Manufacturing Engineering,1999,123(2):94-102.
【4】张洪杰,孟健,唐定骧.高性能镁-稀土结构材料的研制、开发与应用[J].中国稀土学报,2004,22(1):40-47.
【5】刘正,张奎,曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002:16-28.
【6】陈振华,严红革,陈吉华.镁合金[M].北京:化学工业出版社,2004:10-20.
【7】黄晓峰,传海军,阎峰云,等.Mg-9Al-1Si 蠕变前后的组织变化及性能[J].机械工程材料,2007,37(7):1-3.
【8】郭德博,覃善华,欧阳义芳,等.Mg2Al二元系的机械合金化研究[J].贵州大学学报,2004,21(3):255-257.
【9】陈振华,陈鼎.机械合金化与固液反应球磨[M].北京:化学工业出版社,2006.
【10】SINGH D,SURYANARAYANA C,MERTUS L,et al.Extended homogeneity range of intermetallic phases in mechanically alloyed Mg2Al alloys[J].Intermetallics,2003,11(4):373-376.
【2】BROWN B.49th annual IMA world magnesium conference[J].Light Metal Age,1992,50(5/6):21-24.
【3】ROBERT B,ARONSON.Materials for the next generation vehicle[J].Manufacturing Engineering,1999,123(2):94-102.
【4】张洪杰,孟健,唐定骧.高性能镁-稀土结构材料的研制、开发与应用[J].中国稀土学报,2004,22(1):40-47.
【5】刘正,张奎,曾小勤.镁基轻质合金理论基础及其应用[M].北京:机械工业出版社,2002:16-28.
【6】陈振华,严红革,陈吉华.镁合金[M].北京:化学工业出版社,2004:10-20.
【7】黄晓峰,传海军,阎峰云,等.Mg-9Al-1Si 蠕变前后的组织变化及性能[J].机械工程材料,2007,37(7):1-3.
【8】郭德博,覃善华,欧阳义芳,等.Mg2Al二元系的机械合金化研究[J].贵州大学学报,2004,21(3):255-257.
【9】陈振华,陈鼎.机械合金化与固液反应球磨[M].北京:化学工业出版社,2006.
【10】SINGH D,SURYANARAYANA C,MERTUS L,et al.Extended homogeneity range of intermetallic phases in mechanically alloyed Mg2Al alloys[J].Intermetallics,2003,11(4):373-376.
相关信息