SAF2205双相不锈钢与16MnR钢焊接接头的组织与性能
Microstructure and Properties of Welding Joint between SAF2205 Duplex Stainless Steel and 16MnR Steel
摘 要
采用ER309焊丝对SAF2205双相不锈钢与16MnR低合金高强钢进行了钨极氩弧焊(TIG)焊接,对其接头进行了拉伸试验、冲击试验及硬度测试,并用扫描电镜、光学显微镜及X射线衍射仪对接头的显微组织进行了分析.结果表明:母材16MnR钢一侧与焊缝结合界面处分别存在一个脱碳层和增碳层,焊缝中心区为奥氏体+针状铁素体组织;拉伸试样断裂在强度相对较低的母材16MnR钢一侧;在16MnR钢/焊缝界面部位存在硬度突变;接头质量较高,其力学性能能够满足一般工程结构的要求.
异种金属
焊接
显微组织
力学性能
duplex stainless steel
dissimilar metal
welding
microstructure
mechanical property
Abstract
The weld between SAF2205 duplex stainless steel and 16MnR low alloy high strength steel was jointed using tungsten inert gas arc welding (TIG) with ER309 welding wire.The tensile test,impact test and hardness measurement were carried out for the joint.The microstructure of the joint was analyzed by using SEM,optical micnscopy and XRD.The results show that the decarburized layer and carbon-enriched layer were distributed on the side of the 16MnR base metal and in the side of the bonding interface with weld metal,respectively,and the microstructure of austenite and needle-like ferrite was formed in the center of the joint.The fracture of the tensile specimen occurred in the base metal 16MnR with a relatively low strength,and the microhardness of the joint was changed quickly at the interface of 16MnR steel/welal metal.The dissimilar metal welded joint had high quality and could meet the requirements of mechanical properties for engineering structures.
中图分类号 TG444.7
所属栏目 试验研究
基金项目
收稿日期 2009/5/15
修改稿日期 2010/3/19
网络出版日期
作者单位点击查看
备注马启慧(1982-),男,湖北黄冈人,硕士研究生.
引用该论文: MA Qi-hui,WANG Shao-gang,LI Yan,ZHANG Liang. Microstructure and Properties of Welding Joint between SAF2205 Duplex Stainless Steel and 16MnR Steel[J]. Materials for mechancial engineering, 2010, 34(6): 17～20
马启慧,王少刚,李燕,张亮. SAF2205双相不锈钢与16MnR钢焊接接头的组织与性能[J]. 机械工程材料, 2010, 34(6): 17～20
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李伟,栗卓新,李国栋,等.国内外双相不锈钢焊接的研究进展[J].焊接,2007(1):11-15.
【2】SANTOS I O,ZHANG W,GONCCALVES V M,et al.Weld bonding of stainless steel[J].International Journal of Machine Tools & Manufacture,2004,44(14):1431-1439.
【3】韩志诚,王少刚,胡经洪,等.焊接工艺对2205 双相不锈钢接头组织与性能的影响[J].材料工程,2008(8):48-51.
【4】陈建华,陈泽盘,钟玉,等.13MnNiMo54与20MnMo钢焊接接头组织性能研究[J].电焊机,2007,37(12):40-43.
【5】MCPHERSON N A,CHI K,MCLEAN M S,et al.Structure and properties of carbon steel to duplex stainless steel submerged arc welds[J].Materials Science and Technology,2003,19(2):219-226.
【6】RAJEEV R I,SAMAJDAR R,RAMAN R,et al.Origin of hard and soft zone formation during cladding of austenitic/duplex stainless steel on plain carbon steel[J].Materials Science and Technology,2001,17(2):1005-1011.
【7】MUTHUPANDI V,SRINIVASAN P B,SHANKA V,et al.Effect of nickel and nitrogen addition on the microstructure and mechanical properties of power beam processed duplex stainless steel(UNS 31803) weld metals[J].Materials Letters,2005,59(18):2305-2309.
【2】SANTOS I O,ZHANG W,GONCCALVES V M,et al.Weld bonding of stainless steel[J].International Journal of Machine Tools & Manufacture,2004,44(14):1431-1439.
【3】韩志诚,王少刚,胡经洪,等.焊接工艺对2205 双相不锈钢接头组织与性能的影响[J].材料工程,2008(8):48-51.
【4】陈建华,陈泽盘,钟玉,等.13MnNiMo54与20MnMo钢焊接接头组织性能研究[J].电焊机,2007,37(12):40-43.
【5】MCPHERSON N A,CHI K,MCLEAN M S,et al.Structure and properties of carbon steel to duplex stainless steel submerged arc welds[J].Materials Science and Technology,2003,19(2):219-226.
【6】RAJEEV R I,SAMAJDAR R,RAMAN R,et al.Origin of hard and soft zone formation during cladding of austenitic/duplex stainless steel on plain carbon steel[J].Materials Science and Technology,2001,17(2):1005-1011.
【7】MUTHUPANDI V,SRINIVASAN P B,SHANKA V,et al.Effect of nickel and nitrogen addition on the microstructure and mechanical properties of power beam processed duplex stainless steel(UNS 31803) weld metals[J].Materials Letters,2005,59(18):2305-2309.
相关信息