钻杆接头外螺纹加工开裂原因分析
Cracking Analysis of Fillet of Tool Joint Pins during Thread Machining
摘 要
某公司生产的钻杆接头外螺纹在加工时出现裂纹,采用显微组织观察对开裂原因进行了分析.结果表明:该接头外螺纹开裂的主要原因是碳化物的聚集偏析造成锻造过程中偏析区产生组织过热现象,碳化物尖端和基体的结合部位由于热应力和机械应力产生的应力集中而萌生裂纹源,并在随后的变形过程中形成裂纹导致开裂.
碳化物
偏析
过热
裂纹
thread
carbide
precipitation
overheating
crack
Abstract
The cracks were found during machining the external threads of some fillet of tool joint pins.Microstructure observation was used to analyze the cracking cause.The results show that the main cracking reason was that the precipitation of carbides caused microstructure overheating in the precipitation during forging.The cracks generated in the bonding position between tops of carbides and matrix resulting from the stress concentration of heat stress and machining stress,and then formed cracks during deformation.
中图分类号 TG115.5
所属栏目 失效分析
基金项目
收稿日期 2009/5/29
修改稿日期 2009/6/25
网络出版日期
作者单位点击查看
备注巴发海(1966-),男,河南郑州人,博士.
引用该论文: BA Fa-hai,LU Zhou,LI Ling. Cracking Analysis of Fillet of Tool Joint Pins during Thread Machining[J]. Materials for mechancial engineering, 2010, 34(6): 83～84
巴发海,陆洲,李玲. 钻杆接头外螺纹加工开裂原因分析[J]. 机械工程材料, 2010, 34(6): 83～84
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国机械工程学会热处理学会,《金属热处理手册》编委会.金属热处理手册:热处理质量控制和检验[M].北京:机械工业出版社,2002:175-177.
【2】孙盛玉,戴雅康.热处理裂纹分析图谱[M].大连:大连出版社,2002:111.
【3】陶达天.金相检验实例[M].北京:机械工业出版社,1983:95-114.
【4】机械工业理化检验人员培训教材.金相检验[M].上海:上海科学普及出版社,2003:104.
【2】孙盛玉,戴雅康.热处理裂纹分析图谱[M].大连:大连出版社,2002:111.
【3】陶达天.金相检验实例[M].北京:机械工业出版社,1983:95-114.
【4】机械工业理化检验人员培训教材.金相检验[M].上海:上海科学普及出版社,2003:104.
相关信息