High Temperature Plasticity of Continuous Casting Slabs for K60 and X80 Pipeline Steels
摘 要
采用Gleeble 1500型热模拟试验机研究了K60、X80管线钢连铸坯在1 350~650℃、1.0×10-3 s-1应变速率下拉伸时的高温塑性.结果表明:两种钢坯的第Ⅰ脆性区间为熔点~1 300℃;在高温区1 300~900℃时两种钢的塑性均很好,没有产生明显脆化;第Ⅲ脆性区间为900~700℃,该区域可分为γ单相区和γ+α两相区两部分.
Abstract
The high temperature plasticities of continuous casting slabs for K60 and X80 pipeline steels were studied by Gleeble 1500 thermomechanical simulator in the temperature range 1 350℃ to 650℃ at a low strain rate of 1.0×10-3 s-1.The results show that the embrittlement region Ⅰ of the two steel slabs was between melting point and 1 300℃.In the high temperature range(between 1 300℃ and 900℃),the plasticities of both the steels were excellent and there was no evident embrittlement.The embrittlement temperature region III was between 900℃ and 700℃,Which was consist of single γ phase region and γ+α phase region.
中图分类号 TG124.14
所属栏目 材料性能及其应用
基金项目
收稿日期 2009/4/16
修改稿日期 2009/10/23
网络出版日期
作者单位点击查看
备注张双平(1983-),男,江西上饶人,硕士研究生.
引用该论文: ZHANG Shuang-ping,LIU Jing,ZHANG Yan,ZHANG Bei,HAN Jing-tao,PENG Jie. High Temperature Plasticity of Continuous Casting Slabs for K60 and X80 Pipeline Steels[J]. Materials for mechancial engineering, 2010, 34(7): 49~51
张双平,刘靖,张艳,张备,韩静涛,彭杰. K60、X80管线钢连铸坯的高温塑性[J]. 机械工程材料, 2010, 34(7): 49~51
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】毛新平,陈麒琳,朱达炎.薄板坯连铸连轧微合金化技术发展现状[J].钢铁,2008,43(4):1-9.
【2】魏立国,朱岩,徐国栋,等.宝钢厚板边裂成因分析和改善[J].宝钢技术,2006(6):47-50.
【3】MINTZ B,ARROWSMITH J M.Hot-ductility behavior of C-Mn-Nb-Al steels and its relationship to crack propagation during the straightening of continuously cast strand[J].Metals Technology,1979,6(1):24-32.
【4】MINTZ B,YUE S,JONAS J J.Hot ductility of steels and its relationship to the problem of transverse cracking during continuous casting[J].International Materials Reviews,1991,36(5):187-217.
【5】SUZUKI H G,NISHIMURA S,YAMAGUCHI S.Characteristics of embrittlement in steels above 600℃[J].Journal of the Iron and Steel Institute of Japan,1979,65(14):2038-2046.
【6】SUZUKI H G,NISHIMURA S,NAKAMURA Y.Improvement of hot ductility of continuously cast carbon steels[J].Transactions of the Iron and Steel Institute of Japan,1984,24(1):54-59.
【7】王新华,昌波,李景捷,等.700~1000℃间含Nb钢铸坯的延塑性降低与Nb(C,N)析出[J].金属学报,1997,33(5):485-491.
【8】王新华,刘新宇,吕文景,等.含Nb、V、Ti钢连铸坯中碳、氮化物的析出及钢的高温塑性[J].钢铁研究学报,1998,10(6):32-36.
【9】刘洋,王新华,颜涛,等.高性能管线钢高温延塑性对比研究[J].炼钢,2008,24(3):46-49.
【10】赵河山,李殿中,刘朝霞,等.低碳钢形变诱导铁素体相中碳原子的扩散与稳定性研究[J].金属学报,2007,43(3):286-290.
【2】魏立国,朱岩,徐国栋,等.宝钢厚板边裂成因分析和改善[J].宝钢技术,2006(6):47-50.
【3】MINTZ B,ARROWSMITH J M.Hot-ductility behavior of C-Mn-Nb-Al steels and its relationship to crack propagation during the straightening of continuously cast strand[J].Metals Technology,1979,6(1):24-32.
【4】MINTZ B,YUE S,JONAS J J.Hot ductility of steels and its relationship to the problem of transverse cracking during continuous casting[J].International Materials Reviews,1991,36(5):187-217.
【5】SUZUKI H G,NISHIMURA S,YAMAGUCHI S.Characteristics of embrittlement in steels above 600℃[J].Journal of the Iron and Steel Institute of Japan,1979,65(14):2038-2046.
【6】SUZUKI H G,NISHIMURA S,NAKAMURA Y.Improvement of hot ductility of continuously cast carbon steels[J].Transactions of the Iron and Steel Institute of Japan,1984,24(1):54-59.
【7】王新华,昌波,李景捷,等.700~1000℃间含Nb钢铸坯的延塑性降低与Nb(C,N)析出[J].金属学报,1997,33(5):485-491.
【8】王新华,刘新宇,吕文景,等.含Nb、V、Ti钢连铸坯中碳、氮化物的析出及钢的高温塑性[J].钢铁研究学报,1998,10(6):32-36.
【9】刘洋,王新华,颜涛,等.高性能管线钢高温延塑性对比研究[J].炼钢,2008,24(3):46-49.
【10】赵河山,李殿中,刘朝霞,等.低碳钢形变诱导铁素体相中碳原子的扩散与稳定性研究[J].金属学报,2007,43(3):286-290.
相关信息