A Non-quenched and Tempered Bainitic Steel with High Strength-Toughness and Hardenability
摘 要
开发了一种高强韧性高淬透性贝氏体型非调质钢;对该钢的显微组织、力学性能和连续冷却转变(CCT)曲线进行了研究,并与42CrMo钢进行了强韧性比较.结果表明:试验钢在锻后空冷和砂冷后都得到贝氏体组织,强韧性接近;该钢具有良好的淬透性及较宽的贝氏体转变区,在低于0.05℃·s-1的冷却速率下才有少量铁素体析出;在350℃回火2 h后,其力学性能超过了传统调质钢42CrMo的水平.
Abstract
A non-quenched and tempered bainitic steel with high strength-toughness and hardenability had been developed.The microstructure,mechanical properties and continuous cooling transformation (CCT) curves of the steel were studied,and its strength-toughness was compared with that of the 42CrMo steel.The results show that both the tested steels microstructure cooled at air and sand after forging was bainite and the strength-toughness was similar.The steel had good hardenalility and broad bainitic transformation.The ferrite did not appear as the cooling rate was lower than 0.05℃·s-1.The mechanical properties of the bainitic steel were better than those of traditional quenched and tempered steel 42CrMo after tempered at 350℃ for 2 h.
中图分类号 TG142.2
所属栏目 新材料 新工艺
基金项目 先进钢铁材料技术国家工程研究中心课题(D.09-0110-07-002)
收稿日期 2008/9/21
修改稿日期 2009/5/20
网络出版日期
作者单位点击查看
备注彭金明(1983-),男,湖北武汉人,硕士研究生.
引用该论文: PENG Jin-ming,LUO Yi,WANG Hong-bin,WU Xiao-chun. A Non-quenched and Tempered Bainitic Steel with High Strength-Toughness and Hardenability[J]. Materials for mechancial engineering, 2010, 34(8): 33~35
彭金明,罗毅,汪宏斌,吴晓春. 一种高强韧性高淬透性贝氏体型非调质钢[J]. 机械工程材料, 2010, 34(8): 33~35
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵丽萍,于春海,段锐.非调质钢分类的研究[J].吉林农业大学学报,1999,21(4):78-80,84.
【2】张跃,黄运华,翟浩,等.一种新型高性能非调质钢[J].钢铁研究学报,2005,17(2):52-56.
【3】黄维刚,方鸿生,郑燕康.硅和少量钼对Mn-B系贝氏体钢转变动力学的影响[J].金属热处理,1997(10):25-28.
【4】赵捷.粒状贝氏体中残余奥氏体稳定性与强韧性关系[J].机械工程材料,1994,18(5):12-16.
【5】LUO Yi,PENG Jin-min,WANG Hong-bin,et al.Effect of tempering on microstructure and mechanical properties of a non-quenched bainitic steel[J].Material Science and Engineering A,2010,527:3433-3437.
【2】张跃,黄运华,翟浩,等.一种新型高性能非调质钢[J].钢铁研究学报,2005,17(2):52-56.
【3】黄维刚,方鸿生,郑燕康.硅和少量钼对Mn-B系贝氏体钢转变动力学的影响[J].金属热处理,1997(10):25-28.
【4】赵捷.粒状贝氏体中残余奥氏体稳定性与强韧性关系[J].机械工程材料,1994,18(5):12-16.
【5】LUO Yi,PENG Jin-min,WANG Hong-bin,et al.Effect of tempering on microstructure and mechanical properties of a non-quenched bainitic steel[J].Material Science and Engineering A,2010,527:3433-3437.
相关信息