Effect of Surface Mechanical Treatment on Surface Morphology and Tensile Properties of 5083 Aluminum Alloy
摘 要
采用扫描电镜结合慢应变拉伸试验研究了表面机械处理(喷砂和砂轮盘打磨)对5083铝合金的表面形貌和拉伸性能的影响.结果表明:5083铝合金经表面机械处理后,出现了一定程度的损伤(表层产生了裂纹),从而使其拉伸时断裂时间缩短和伸长率降低,其中表面喷砂后,伸长率降低了9.9%,表面打磨后,伸长率降低了13.5%.
Abstract
Scan electron microscopy and slow strain tension test were utilized to study the effect of surface mechanical treatment (sand blast and hand polish) on surface morphology and tensile properties of the 5083 aluminum alloy.The results show that surface mechanical treatment could lead to the damage of 5083 aluminum alloy(micro-cracks occured on the surface)in a certain extent,and the micro-cracks could lead to the shertening of the fracture time and the decrease of elongation during tension.The elongation of the sand blast-treated aluminum alloy decreased by 9.9%,and that of the hand polish-treated aluminum alloy decreased by 13.5%.
中图分类号 TB302
所属栏目 试验研究
基金项目
收稿日期 2009/8/18
修改稿日期 2010/4/27
网络出版日期
作者单位点击查看
备注林红吉(1973-),男,辽宁沈阳人,工程师,硕士.
引用该论文: LIN Hong-ji,MENG Xian-lin,CAO Jing-yi,ZHANG Hai-yong. Effect of Surface Mechanical Treatment on Surface Morphology and Tensile Properties of 5083 Aluminum Alloy[J]. Materials for mechancial engineering, 2010, 34(10): 25~27
林红吉,孟宪林,曹京宜,张海永. 表面机械处理对5083铝合金表面形貌和拉伸性能的影响[J]. 机械工程材料, 2010, 34(10): 25~27
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王祝堂,田荣璋.铝合金及其加工手册[M].长沙:中南大学出版社,2000:240-250.
【2】CHEN H H,WANG J Y,LEE J,et al.Superplasticity of AA5083 alloy as processed by equal channel angular extrusion[J].Journal of Alloys and Compounds,2008,460(1/2):305-308.
【3】鲍戈拉德.海船的腐蚀与保护[M].北京:国防工业出版社,1990:93-102.
【4】SEARLES J L,GOUM P I,BUCHHEIT R G.Stress corrosion cracking of sensitized AA5083 (Al-4.5Mg-1.0Mn)[J].Materials Science Forum,2002,396/402:1437-1442.
【5】赵月红,林乐耘.不同加工及表面处理状态LF6铝镁合金的深海腐蚀行为[J].中国有色金属学报,2001(11):27-30.
【6】黎完模,宋玉苏,邓淑珍.涂装金属的腐蚀[M].长沙:国防科技大学出版社,2003:168.
【7】TONSHOFF H K,DENKENA B,REIEMUT H.Influence of thermal mechanical impacts on fatigue in precision grinding[C]//Advancing in Surface Treatment.Oxford:Pergamon Press,1985:387-392.
【8】BRINKSMEIER E,ECKEBRECHT J.Residual stress-mea-surement and causes in machining processes[J].International Institution for Production Engineering Research,1982,31(1):491-509.
【9】ABALLE A,BETHENCOURT M,BOTANA F J,et al.Influence of the degree of polishing of alloy AA5083 on its behaviour against localised alkaline corrosion[J].Corrosion Science,2004,46(8):1909-1920.
【10】AFSETH A,NORDLIEN J H,SCAMANS G M,et al.Influence of heat treatment and surface conditioning on filiform corrosion of aluminium alloys AA3005 and AA5754[J].Corrosion Science,2001,43(12):2359-2377.
【11】ZHOU X,THOMPSON G,SCAMANS G M.The influence of surface treatment on filiform corrosion resistance of painted aluminium alloy sheet[J].Corrosion Science,2003,45(8):1767-1777.
【12】王荣,郑修麟.铝合金中腐蚀疲劳裂纹的起始与扩展[J].机械工程材料,1995,19(3):5-7.
【2】CHEN H H,WANG J Y,LEE J,et al.Superplasticity of AA5083 alloy as processed by equal channel angular extrusion[J].Journal of Alloys and Compounds,2008,460(1/2):305-308.
【3】鲍戈拉德.海船的腐蚀与保护[M].北京:国防工业出版社,1990:93-102.
【4】SEARLES J L,GOUM P I,BUCHHEIT R G.Stress corrosion cracking of sensitized AA5083 (Al-4.5Mg-1.0Mn)[J].Materials Science Forum,2002,396/402:1437-1442.
【5】赵月红,林乐耘.不同加工及表面处理状态LF6铝镁合金的深海腐蚀行为[J].中国有色金属学报,2001(11):27-30.
【6】黎完模,宋玉苏,邓淑珍.涂装金属的腐蚀[M].长沙:国防科技大学出版社,2003:168.
【7】TONSHOFF H K,DENKENA B,REIEMUT H.Influence of thermal mechanical impacts on fatigue in precision grinding[C]//Advancing in Surface Treatment.Oxford:Pergamon Press,1985:387-392.
【8】BRINKSMEIER E,ECKEBRECHT J.Residual stress-mea-surement and causes in machining processes[J].International Institution for Production Engineering Research,1982,31(1):491-509.
【9】ABALLE A,BETHENCOURT M,BOTANA F J,et al.Influence of the degree of polishing of alloy AA5083 on its behaviour against localised alkaline corrosion[J].Corrosion Science,2004,46(8):1909-1920.
【10】AFSETH A,NORDLIEN J H,SCAMANS G M,et al.Influence of heat treatment and surface conditioning on filiform corrosion of aluminium alloys AA3005 and AA5754[J].Corrosion Science,2001,43(12):2359-2377.
【11】ZHOU X,THOMPSON G,SCAMANS G M.The influence of surface treatment on filiform corrosion resistance of painted aluminium alloy sheet[J].Corrosion Science,2003,45(8):1767-1777.
【12】王荣,郑修麟.铝合金中腐蚀疲劳裂纹的起始与扩展[J].机械工程材料,1995,19(3):5-7.
相关信息