Na2O含量对包钢稀选尾矿制备微晶玻璃析晶行为和性能的影响
Effect of Na2O Content on Crystallization Behavior and Properties of Glass-Ceramics Prepared by Utilizing Tailing of BISCO
摘 要
采用DSC、XRD、SEM等方法研究了Na2O含量对以包钢稀选尾矿为主料制备微晶玻璃析晶行为及性能的影响.结果表明:随着Na2O含量的增加,微晶玻璃的晶化温度逐渐降低;当Na2O质量分数大于6.7%时,主晶相由钙铁辉石变为霞石;当Na2O质量分数为3.6%时,微晶玻璃的抗弯强度最大为150.4 MPa,密度最大为3.4 g·cm-3.
尾矿
微晶玻璃
性能
Na2O
tailing
glass-ceramic
property
Abstract
The Effect of Na2O content on crystallization behavior and properties of glass-ceramics preparing by utilizing tailing of BISCO was studied by means of DSC,XRD,SEM.The results show that with the increase of Na2O content the crystallization temperature of the glass-ceramics decreased.When the Na2O content was larger than 6.7wt% the main crystal phases changed from hedenbergite to nepheline.When the Na2O content was 36wt%,the maximum bending strength of the glass-ceramics was 150.4 MPa,and the maximum density was 3.4 g·cm-3.
中图分类号 TQ171
所属栏目 试验研究
基金项目 包头市重大科技攻关项目(2004z007)
收稿日期 2009/10/19
修改稿日期 2010/6/3
网络出版日期
作者单位点击查看
备注朱静(1983-),女,江苏徐州人,硕士研究生.
引用该论文: ZHU Jing,ZHAO Tuan,GAO Zhan-yong,LI Bao-wei,LI Jie. Effect of Na2O Content on Crystallization Behavior and Properties of Glass-Ceramics Prepared by Utilizing Tailing of BISCO[J]. Materials for mechancial engineering, 2010, 34(11): 27～30
朱静,赵团,高占勇,李保卫,李解. Na2O含量对包钢稀选尾矿制备微晶玻璃析晶行为和性能的影响[J]. 机械工程材料, 2010, 34(11): 27～30
被引情况:
【1】李保卫,杜永胜,张雪峰,贾晓林,赵鸣,陈华,邓磊波, "钙铝质量比对矿渣微晶玻璃结构及性能的影响",机械工程材料 36, 46-49(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】林东鲁,李春龙,邬虎林.白云鄂博特殊矿采冶工艺攻关与技术进步[M].北京:冶金工业出版社,2007:113-115.
【2】陈吉春.矿业尾矿微晶玻璃制品的开发利用[J].中国矿业,2005,14(5):83-88.
【3】杨家宽,肖波,王秀萍.利用钢铁炉渣制备微晶玻璃技术[J].有色金属,2003,55(3):130-133.
【4】TULYAGANOV D U,RIBEIRO M J,LABRINCHA J A.Development of glass-ceramics by sintering and crystallization of fine powders of calcium-magnesium-aluminosilicate glass[J].Ceramics International,2002,28:515-520.
【5】西北轻工业学院.玻璃工艺学[M].北京:中国轻工业出版社,1983:16-23.
【6】陈金方.玻璃电熔化与电加热[M].上海:华东理工大学出版社,2002:7.
【7】程金树,何峰,袁坚,等.氧化钙对烧结法建筑装饰微晶玻璃烧结过程的影响[J].武汉工业大学学报,1997,19(4):1-4.
【8】陆雷,江勤,张乐军,等.ZnO添加剂对复合尾矿微晶玻璃的性能及显微结构的影响[J].矿产综合利用,2007(2):22-25.
【9】何峰,杜勇,王平,等.B2O3对锂铝硅系统微晶玻璃结构性能的影响[J].武汉理工大学学报,2007,29(6):1-4.
【10】李斌,文丽华,马臣.Fe2O3对CaO-SiO2玻璃和微晶玻璃性能的影响[J].陶瓷学报,2007,28(2):99-103.
【11】张小福,卢安贤,张红霞.Na2O加入量对Li2O-ZnO-SiO2微晶玻璃性能的影响[J].超硬材料工程,2007,19(4):27-32.
【12】MCMILLAN P W.Glass ceramics[M].New York:Acade-mic Press,1979.
【13】顾幸勇,陈玉清.陶瓷制品检测及缺陷分析[M].北京:化学工业出版社,2006:211.
【14】史培阳,姜茂发,刘承军.用铁尾矿、硼泥和粉煤灰制备微晶玻璃[J].钢铁研究学报,2005,17(5):22-30.
【15】MENG Q G,ZHANG S G,LI J G,et al.Strong liquid behavior of Pr55Ni25Al20 bulk metallic glass[J].J Alloy Comp,2007,431:191-196.
【16】赵运才,肖汉宁,谭伟.耐磨微晶玻璃的组成与晶化特性的研究[J].硅酸盐通报,2003,31(4):406-409.
【17】HE Feng,DU Yong,XIE Jun-lin,et al.Effect of the cool system on internal stress of CaO-Al2O3-SiO2 glass-ceramic system[J].Journal of Wuhan University of Technology Mater,2007,22(4):760-763.
【18】关振铎.无机材料物理性能[M].北京:清华大学出版社,1992:42-48.
【2】陈吉春.矿业尾矿微晶玻璃制品的开发利用[J].中国矿业,2005,14(5):83-88.
【3】杨家宽,肖波,王秀萍.利用钢铁炉渣制备微晶玻璃技术[J].有色金属,2003,55(3):130-133.
【4】TULYAGANOV D U,RIBEIRO M J,LABRINCHA J A.Development of glass-ceramics by sintering and crystallization of fine powders of calcium-magnesium-aluminosilicate glass[J].Ceramics International,2002,28:515-520.
【5】西北轻工业学院.玻璃工艺学[M].北京:中国轻工业出版社,1983:16-23.
【6】陈金方.玻璃电熔化与电加热[M].上海:华东理工大学出版社,2002:7.
【7】程金树,何峰,袁坚,等.氧化钙对烧结法建筑装饰微晶玻璃烧结过程的影响[J].武汉工业大学学报,1997,19(4):1-4.
【8】陆雷,江勤,张乐军,等.ZnO添加剂对复合尾矿微晶玻璃的性能及显微结构的影响[J].矿产综合利用,2007(2):22-25.
【9】何峰,杜勇,王平,等.B2O3对锂铝硅系统微晶玻璃结构性能的影响[J].武汉理工大学学报,2007,29(6):1-4.
【10】李斌,文丽华,马臣.Fe2O3对CaO-SiO2玻璃和微晶玻璃性能的影响[J].陶瓷学报,2007,28(2):99-103.
【11】张小福,卢安贤,张红霞.Na2O加入量对Li2O-ZnO-SiO2微晶玻璃性能的影响[J].超硬材料工程,2007,19(4):27-32.
【12】MCMILLAN P W.Glass ceramics[M].New York:Acade-mic Press,1979.
【13】顾幸勇,陈玉清.陶瓷制品检测及缺陷分析[M].北京:化学工业出版社,2006:211.
【14】史培阳,姜茂发,刘承军.用铁尾矿、硼泥和粉煤灰制备微晶玻璃[J].钢铁研究学报,2005,17(5):22-30.
【15】MENG Q G,ZHANG S G,LI J G,et al.Strong liquid behavior of Pr55Ni25Al20 bulk metallic glass[J].J Alloy Comp,2007,431:191-196.
【16】赵运才,肖汉宁,谭伟.耐磨微晶玻璃的组成与晶化特性的研究[J].硅酸盐通报,2003,31(4):406-409.
【17】HE Feng,DU Yong,XIE Jun-lin,et al.Effect of the cool system on internal stress of CaO-Al2O3-SiO2 glass-ceramic system[J].Journal of Wuhan University of Technology Mater,2007,22(4):760-763.
【18】关振铎.无机材料物理性能[M].北京:清华大学出版社,1992:42-48.
相关信息