0Cr18Ni9钢表面等离子铌合金化层的显微组织和摩擦磨损性能
Microstructure and Friction and Wear Properties of Plasma Niobium Surface Alloying Layer on 0Cr18Ni9 Steel
摘 要
采用双辉等离子渗金属技术在0Cr18Ni9奥氏体不锈钢表面制备出厚度为22 μm均匀致密的渗铌合金化层;分析了合金化层的成分、显微组织及其摩擦磨损性能.结果表明:铌合金化层主要由铌的碳化物(NbC、Nb6C5)和金属间化合物(Cr2Nb、Fe2Nb)组成,表面硬度较基体提高一倍左右,达到614 HV0.025;合金化层的摩擦因数(8.05×10-2)与基体的(7.97×10-2)基本相同;基体和合金化层均以粘着磨损和磨粒磨损为主要磨损形式,合金化层的磨损率较基体的明显降低.
渗铌合金化层
摩擦磨损性能
austenitic stainless steel
niobium alloying layer
friction and wear property
Abstract
A uniform and compact niobium alloying layer with the thickness of 22 μm was prepared on the 0Cr18Ni9 austenitic stainless steel surface using double-glow plasma surface alloying technology.The composition,microstructure and tribological properties of the alloying layer were examined.The results show that the Nb alloying layer was mainly composed of Nb-containing carbides (NbC,Nb6C5) and intermetallic compounds (Cr2Nb,Fe2Nb).The surface hardness of the alloying layer enhanced by one time compared with that of the substrate,which reached 614 HV0.025.The friction coefficient of the Nb alloying layer (8.05×10-2) and the substrate (7.97×10-2) were roughly same.The main wear mode of both the substrate and alloying layer was a mixture of adhesion and abrasion.The wear rate of the alloying layer decreased obviously compared with that of the substrate.
中图分类号 TG142.7
所属栏目 材料性能及其应用
基金项目 太原市科技项目大学生创新创业专项(08122087);太原理工大学青年基金资助项目;山西省基础研究青年科技研究基金资助项目(2008012008-3);山西省研究生优秀创新项目(20081042)
收稿日期 2009/10/26
修改稿日期 2009/11/27
网络出版日期
作者单位点击查看
备注谢燕翔(1982-),男,陕西榆林人,硕士研究生.
引用该论文: XIE Yan-xiang,WANG Zhen-xia,LIU Jun,HE Zhi-yong. Microstructure and Friction and Wear Properties of Plasma Niobium Surface Alloying Layer on 0Cr18Ni9 Steel[J]. Materials for mechancial engineering, 2010, 34(11): 61～64
谢燕翔,王振霞,刘俊,贺志勇. 0Cr18Ni9钢表面等离子铌合金化层的显微组织和摩擦磨损性能[J]. 机械工程材料, 2010, 34(11): 61～64
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陆世英.腐蚀与防护手册(第二册)[M].北京:化学工业出版社,1990:190-253.
【2】郑海生.奥氏体不锈钢晶间腐蚀问题的研究及防止[J].机电工程与技术,2004,33(1):46-47.
【3】王荣滨.18-8型奥氏体不锈钢的晶间腐蚀[J].上海钢研,2003(2):19-21.
【4】屈兴胜,林成,刘志林.奥氏体不锈钢晶间腐蚀[J].辽宁工学院学报,2007,27(2):45-47.
【5】罗宏,龚敏.奥氏体不锈钢的晶间腐蚀[J].腐蚀科学与防护技术,2006,18(5):357-360.
【6】谢燕翔,刘俊,王振霞,等.0Cr18Ni9钢表面等离子铌合金的及改性层抗晶间腐蚀性能的研究[J].热加工工艺,2009,38(4):71-73.
【7】王俊琴.铌在不锈钢中的应用[J].太钢科技,2003(3):23-26.
【8】贲海峰.TiAl基合金表面改性层组织与性能研究[D].太原:太原理工大学,2006.
【9】BROSZIT E,MOATTHES B,HERR W,et al.Tri-biological properties of r.f.sputtered Ti-B-C coatings under various pin-on-disc wear test conditions[J].Surface and CoatingsTechnology,1993,58:29-35.
【2】郑海生.奥氏体不锈钢晶间腐蚀问题的研究及防止[J].机电工程与技术,2004,33(1):46-47.
【3】王荣滨.18-8型奥氏体不锈钢的晶间腐蚀[J].上海钢研,2003(2):19-21.
【4】屈兴胜,林成,刘志林.奥氏体不锈钢晶间腐蚀[J].辽宁工学院学报,2007,27(2):45-47.
【5】罗宏,龚敏.奥氏体不锈钢的晶间腐蚀[J].腐蚀科学与防护技术,2006,18(5):357-360.
【6】谢燕翔,刘俊,王振霞,等.0Cr18Ni9钢表面等离子铌合金的及改性层抗晶间腐蚀性能的研究[J].热加工工艺,2009,38(4):71-73.
【7】王俊琴.铌在不锈钢中的应用[J].太钢科技,2003(3):23-26.
【8】贲海峰.TiAl基合金表面改性层组织与性能研究[D].太原:太原理工大学,2006.
【9】BROSZIT E,MOATTHES B,HERR W,et al.Tri-biological properties of r.f.sputtered Ti-B-C coatings under various pin-on-disc wear test conditions[J].Surface and CoatingsTechnology,1993,58:29-35.
相关信息