45钢疲劳裂纹尖端渗注不同镀液对裂纹扩展速率的影响
Effects of Different Plating Solutions Permeating into Fatigue Crack Tip on Crack Growth Rate of 45 Steel
摘 要
研究了在45钢疲劳裂纹尖端渗注不同镀液对该疲劳裂纹扩展速率的影响,并采用扫描电镜和能谱仪对渗注镀液后裂纹尖端的形貌和成分进行了分析.结果表明:当应力强度因子幅值ΔK一定时,两种镀液渗注后的45钢疲劳裂纹扩展速率均比未渗注的大幅降低;随着时间的延长,渗注镀液后45钢疲劳裂纹扩展速率先降低然后趋于稳定;镀液可有效渗注到疲劳裂纹尖端,且磷化液的止裂效果优于镀镍液的.
镀液
疲劳裂纹扩展速率
裂纹闭合
45 steel
plating solution
fatigue crack growth rate
crack closure
Abstract
Effects of different plating solutions permeating into fatigue crack tip on the crack growth rate of the 45 steel were investigated.The morphology and component of the fatigue crack tip after the solution permeating were analyzed by means of SEM and EDS.The results indicate that the crack growth rate of the 45 steel deposited with the two plating solutions was obviously lower than that of the one without deposition when the stress intensity factor amplitude ΔK was invariable.With the prolongation of time,the crack growth rate of the 45 steel after deposition first decreased then tended to be steady.The solution could effectively permeated into the fatigue crack tips.The crack arrest effect of the phosphate plating solution was better than that of the nickel plating solution.
中图分类号 TG115.5
所属栏目 试验研究
基金项目 江苏省高校自然科学基础研究项目(07KJB430036);南京工程学院基金项目(KXJ08003;KXJ08053;KXG08138)
收稿日期 2010/1/15
修改稿日期 2010/9/16
网络出版日期
作者单位点击查看
备注白允强(1979-),男,山东聊城人,讲师,博士.
引用该论文: BAI Yun-qiang,WANG Zhang-zhong,HE Xian-cong,ZHOU Heng-zhi,BA Zhi-xin. Effects of Different Plating Solutions Permeating into Fatigue Crack Tip on Crack Growth Rate of 45 Steel[J]. Materials for mechancial engineering, 2010, 34(12): 22～24
白允强,王章忠,贺显聪,周衡志,巴志新. 45钢疲劳裂纹尖端渗注不同镀液对裂纹扩展速率的影响[J]. 机械工程材料, 2010, 34(12): 22～24
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】范华林,陈平.电磁热效应理论在薄板止裂技术上的应用[J].兵工学报,2005,26(6):791-794.
【2】肖福仁,白象忠,乔桂英,等.电磁热效应对35钢裂纹尖端组织及止裂效果的影响[J].材料热处理学报,2001,22(2):56-59.
【3】沙桂英,刘瑞堂,刘殿魁,等.应力波加载条件下907A钢-20 ℃时的动态断裂与止裂研究[J].哈尔滨工程大学学报,2001,22(1):96-101.
【4】张卫国,田洪,宓为建,等.应力比r对构件疲劳裂纹扩展的影响分析[J].中国工程机械学报,2008,6(4):403-408.
【5】ISHIARA S,GOSHIMA T.The influence of the stress ratio on fatigue crack growth in a cermet[J].Journal of Materials Science,2000,35(22):5661-5665.
【6】任爱国,王晓静,丁静.激光熔覆止裂技术研究[J].表面技术,2006,35(2):69-81.
【7】SHIN C S,CAI C Q.A model for evaluating the effect of fatigue crack repair by the infiltration method[J].Fatigue & Fracture of Engineering Materials & Structures,2000,23(10):835-845.
【8】银建中,王炎炎.压力容器疲劳止裂技术——“人工楔块”止裂方法的研究[J].化工机械,1997,24(3):139-163.
【9】龚磊,邹军.低温化学镀镍-磷合金工艺的研究[J].江西农业大学学报,2004,26(2):318-320.
【10】于取民.清洁型常温锌系磷化液研究[J].材料保护,2006,39(5):26-29.
【11】王章忠.应变片位置对测定裂纹闭合灵敏度的影响[J].理化检验-物理分册,1999,35(8):342-344.
【2】肖福仁,白象忠,乔桂英,等.电磁热效应对35钢裂纹尖端组织及止裂效果的影响[J].材料热处理学报,2001,22(2):56-59.
【3】沙桂英,刘瑞堂,刘殿魁,等.应力波加载条件下907A钢-20 ℃时的动态断裂与止裂研究[J].哈尔滨工程大学学报,2001,22(1):96-101.
【4】张卫国,田洪,宓为建,等.应力比r对构件疲劳裂纹扩展的影响分析[J].中国工程机械学报,2008,6(4):403-408.
【5】ISHIARA S,GOSHIMA T.The influence of the stress ratio on fatigue crack growth in a cermet[J].Journal of Materials Science,2000,35(22):5661-5665.
【6】任爱国,王晓静,丁静.激光熔覆止裂技术研究[J].表面技术,2006,35(2):69-81.
【7】SHIN C S,CAI C Q.A model for evaluating the effect of fatigue crack repair by the infiltration method[J].Fatigue & Fracture of Engineering Materials & Structures,2000,23(10):835-845.
【8】银建中,王炎炎.压力容器疲劳止裂技术——“人工楔块”止裂方法的研究[J].化工机械,1997,24(3):139-163.
【9】龚磊,邹军.低温化学镀镍-磷合金工艺的研究[J].江西农业大学学报,2004,26(2):318-320.
【10】于取民.清洁型常温锌系磷化液研究[J].材料保护,2006,39(5):26-29.
【11】王章忠.应变片位置对测定裂纹闭合灵敏度的影响[J].理化检验-物理分册,1999,35(8):342-344.
相关信息