电化学充氢条件下夹杂物对管线钢氢致开裂敏感性的影响
Effect of Inclusions on Hydrogen Induced Cracking Susceptibility of Pipeline Steels under Electrochemical Hydrogen-Charging Condition
摘 要
对X52、20、X70管线钢在0.5 mol·L-1 H2SO4 溶液中进行电化学充氢试验, 研究了钢中夹杂物形态、大小、数量、分布对管线钢氢致开裂(HIC)的影响。结果表明: X52钢的HIC敏感性远小于20钢和X70钢的; 20钢中的MnS夹杂物并不是氢致裂纹的必然形核位置, 而Al2O3、复合氧化物/铁的碳化物、硅夹杂物则是更为有害的氢致裂纹源; X70钢中以Al2O3、铁的碳化物造成的氢致开裂危害最大; 相邻夹杂物形成的裂纹源不断扩展并合成了更大的裂纹。
充氢
氢致开裂
夹杂物
pipeline steel
hydrogen-charging
hydrogen induced cracking
inclusion
Abstract
Effect of morphology, size, quantity and distribution of inclusions on hydrogen induced cracking (HIC) of pipeline steels X52, 20 and X70 were studied in 0.5 mol·L-1 H2SO4 solution. The results show that the HIC sensitivity of X52 pipeline was much less than that of 20 steel and X70 steel. MnS inclusion in 20 steel was no inevitable location for hydrogen induced cracks, and Al2O3, composite oxides/Fe-C and silicon carbide inclusion were more harmful hydrogen induced crack sources. In X70 steel, the harmfulness of HIC induced by Al2O3 and Fe-C inclusion was the most, large cracks formed due to the growth and merging of the crack source at the positions of adjacent inclusions.
中图分类号 TG111.92 DOI 10.11973/jxgccl201509006
所属栏目 试验研究
基金项目 国家科技支撑计划项目(2011BAE25B00, 2011BAE25B03)
收稿日期 2014/1/3
修改稿日期 2015/3/23
网络出版日期
作者单位点击查看
备注胡亮(1986-), 男, 江西吉安人 , 硕士研究生。
引用该论文: HU Liang,CHEN Jian,WANG Bing,LIU Qing-you,LI Zhen-hua. Effect of Inclusions on Hydrogen Induced Cracking Susceptibility of Pipeline Steels under Electrochemical Hydrogen-Charging Condition[J]. Materials for mechancial engineering, 2015, 39(9): 25～31
胡亮,陈健,汪兵,刘清友,黎振华. 电化学充氢条件下夹杂物对管线钢氢致开裂敏感性的影响[J]. 机械工程材料, 2015, 39(9): 25～31
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】XUE H B, CHENG Y F. Characterization of inclusions of X80 pipeline steel and its correlation with hydrogen-induced cracking[J]. Corrosion Science ,2011,53:1201-1208.
【2】杜一俭. 石油化工装置中硫腐蚀机理分析[J]. 科技创新与应用,2012(10):33-34.
【3】刘生,张一认,韩金节, 等.夹杂物对16MnR(HIC)钢板抗氢致开裂的影响[J]. 压力容器, 2001,18(2):20-22.
【4】肖磊,王学林,尚成嘉. 高厚度/直径比的UOE管线钢的耐酸性能[C]//2009管线技术国际会议论文.[出版地不详]: [出版者不详], 2010:72-82.
【5】张颖瑞, 董超芳, 李晓刚, 等.电化学充氢条件下X70管线钢及其焊缝的氢致开裂行为[J].金属学报,2006,42(5):521-527.
【6】DONG C F, LI X G, LIU Z Y, et al. Hydrogen-induced cracking and healing behaviour of X70 steel[J]. Journal of Alloys and Compounds,2009,484:966-972.
【7】魏宝明.金属腐蚀理论及应用[M]. 北京:化学工业出版社,2008:341.
【8】程吉浩.X120管线钢的氢致裂纹与土壤应力腐蚀研究[D].武汉: 武汉科技大学,2011:6-7.
【9】ISHIKAWA N, SHINMIYA T, SHIKANAI N, et al. Recent advance in high strength linepipes for heavy sour service[C]∥The Pipeline Technology Conference in Ostend, Belgium.[S.l]:[s.n.],2009.
【10】邵晓东,庄传晶,韩新利等.酸性环境用油气输送管线钢的研究进展[J].机械工程材料,2010,34(11):1-4.
【11】尹成先. X70管线钢氢致开裂及应力腐蚀行为研究[D].西安: 西安建筑科技大学,2003:38-40.
【12】任学冲,褚武扬,李金许,等.夹杂对氢鼓泡形成的影响[J].金属学报,2007, 43(7):673-677.
【13】镇凡, 刘静, 黄峰,等.夹杂物对高强度管线钢氢致开裂的影响[C]//第五届全国腐蚀大会论文集.[出版地不详]: [出版者不详], 2009: 118-121.
【14】褚武扬.氢损伤与滞后断裂[M].北京: 冶金工业出版社, 1988: 190-255.
【15】张莉萍,葛建国, 赵爱军.浅谈钢中夹杂物的控制对钢质量的影响[J].包钢科技, 2002,28 (4):85-87.
【2】杜一俭. 石油化工装置中硫腐蚀机理分析[J]. 科技创新与应用,2012(10):33-34.
【3】刘生,张一认,韩金节, 等.夹杂物对16MnR(HIC)钢板抗氢致开裂的影响[J]. 压力容器, 2001,18(2):20-22.
【4】肖磊,王学林,尚成嘉. 高厚度/直径比的UOE管线钢的耐酸性能[C]//2009管线技术国际会议论文.[出版地不详]: [出版者不详], 2010:72-82.
【5】张颖瑞, 董超芳, 李晓刚, 等.电化学充氢条件下X70管线钢及其焊缝的氢致开裂行为[J].金属学报,2006,42(5):521-527.
【6】DONG C F, LI X G, LIU Z Y, et al. Hydrogen-induced cracking and healing behaviour of X70 steel[J]. Journal of Alloys and Compounds,2009,484:966-972.
【7】魏宝明.金属腐蚀理论及应用[M]. 北京:化学工业出版社,2008:341.
【8】程吉浩.X120管线钢的氢致裂纹与土壤应力腐蚀研究[D].武汉: 武汉科技大学,2011:6-7.
【9】ISHIKAWA N, SHINMIYA T, SHIKANAI N, et al. Recent advance in high strength linepipes for heavy sour service[C]∥The Pipeline Technology Conference in Ostend, Belgium.[S.l]:[s.n.],2009.
【10】邵晓东,庄传晶,韩新利等.酸性环境用油气输送管线钢的研究进展[J].机械工程材料,2010,34(11):1-4.
【11】尹成先. X70管线钢氢致开裂及应力腐蚀行为研究[D].西安: 西安建筑科技大学,2003:38-40.
【12】任学冲,褚武扬,李金许,等.夹杂对氢鼓泡形成的影响[J].金属学报,2007, 43(7):673-677.
【13】镇凡, 刘静, 黄峰,等.夹杂物对高强度管线钢氢致开裂的影响[C]//第五届全国腐蚀大会论文集.[出版地不详]: [出版者不详], 2009: 118-121.
【14】褚武扬.氢损伤与滞后断裂[M].北京: 冶金工业出版社, 1988: 190-255.
【15】张莉萍,葛建国, 赵爱军.浅谈钢中夹杂物的控制对钢质量的影响[J].包钢科技, 2002,28 (4):85-87.
相关信息