X-Ray Real-Time Imaging Technique for Titanium Alloy Welded Joint
摘 要
通过测定相关质量控制参数,系统地探讨了X射线实时成像与计算机图像处理技术的特点。以钛合金气瓶为例,进行了大量的工艺试验和图像采集。试验结果表明,X射线实时成像所得图像质量的对比度和清晰度可与X射线照相法中的底片质量媲美,缺陷检出效果良好。由此优选出了一套最佳的工艺组合,并验证了系统最佳放大倍数的通用性。
Abstract
The characteristics of related qulity controlling parameters used in real-time X-ray imaging technique and computer image processing technique were discussed. Agreat deal of process trials and images aquisition were proceeded which taking the titanium alloy cylinder as the example. Testing results showed that the contrast and sensitivity of the image getting by X-ray real-time imaging technique was as good as X radiography testing technique. Defect detection rate was satisfied also. The best testing process parameters were got through those trials and the universal property of the max amplifying ratio was proved also.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2007/1/29
修改稿日期
网络出版日期
作者单位点击查看
备注史建军(1970-),男,工程师,无损检测主管检验师,从事航天领域无损检测工作。
引用该论文: SHI Jian-jun. X-Ray Real-Time Imaging Technique for Titanium Alloy Welded Joint[J]. Nondestructive Testing, 2007, 29(8): 469~471
史建军. X射线实时成像技术在钛合金焊缝探伤中的工艺试验研究[J]. 无损检测, 2007, 29(8): 469~471
被引情况:
【1】董方旭,王从科,赵付宝,凡丽梅, "一种碳纤维复合材料X射线穿透曲线的绘制方法",无损检测 38, 30-33(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李 衍.焊缝射线实时成像检测[J].无损检测,1992,14(11):323-323.
【2】BS 7009—1988 焊缝射线实时成像检测应用导则[S].
【3】曾祥照.X射线实时成像实时成像检测技术现场测评方法无损检测[J].2000,22(5):27-28.
【2】BS 7009—1988 焊缝射线实时成像检测应用导则[S].
【3】曾祥照.X射线实时成像实时成像检测技术现场测评方法无损检测[J].2000,22(5):27-28.
相关信息