GH4049合金钨夹杂射线检测工艺研究
The Research of Radiographic Testing Technology for High Temperature Alloy GH4049
摘 要
含钨夹杂的GH4049棒料被加工成叶片等不同的航空零部件。为避免带有钨夹杂的零部件装机使用, 提出了采用射线检测方法对涉及的在制品和成品进行检查。通过分析研究和试验, 证明了射线检测高温合金钨夹杂的可行性, 确立了高温合金钨夹杂零部件的射线检测工艺。
钨夹杂
灵敏度
X-ray Inspection
W inclusion
Sensitivity
Abstract
The bar material of GH4049 containing W inclusion was made for different aero parts such as blade and so on.In order to avoid the parts containing of W inclusion being used in aero-engine, this paper proposed an X-ray inspection method for finished or semi-finished products, and through analysis and test, the feasibility of X-ray inspection to high temperature alloy containing W inclusion was proved. X-ray inspection technology of high temperature parts containing W inclusion was established.
中图分类号 TG115.28
所属栏目 试验研究
基金项目
收稿日期 2009/1/5
修改稿日期
网络出版日期
作者单位点击查看
备注熊瑛(1968-), 女, 高级工程师, 工程硕士, 主任, 多年来一直从事无损检测技术的研究与工程化应用工作。
引用该论文: XIONG Ying,FU Su-Zhen,ZHANG Xiao-Ling. The Research of Radiographic Testing Technology for High Temperature Alloy GH4049[J]. Nondestructive Testing, 2009, 31(2): 125～128
熊瑛,付肃真,张孝玲. GH4049合金钨夹杂射线检测工艺研究[J]. 无损检测, 2009, 31(2): 125～128
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】中国机械工程学会无损检测分会.射线检测[M].北京: 机械工业出版社,1997.
【2】郑世才, 王兰涛.工业射线无损检测技术[M].北京: 中国航天标准化研究所,2001.
【2】郑世才, 王兰涛.工业射线无损检测技术[M].北京: 中国航天标准化研究所,2001.
相关信息