P110石油套管水压试验开裂原因分析
Cracking Reason Analysis of P110 Oil Casing after Hydraulic Test
摘 要
通过对材料的化学成分分析、断口分析及金相检验,对177.8 mm×11.51 mm P110石油套管水压试验后出现的管体异常开裂现象进行分析。结果表明: 导致管体纵向开裂的原因是该套管管体组织内分布着大型夹杂物,它的存在破坏了材料组织的连续性,削弱了横向抗拉强度,在应力集中的条件下,局部应力超过实际的抗拉强度从而产生开裂。
水压试验
夹杂物
连续性
抗拉强度
oil casing
hydraulic test
inclusions
continuity
tensile strength
Abstract
The cracking reason of 177.8 mm × 11.51 mm P110 oil casing after the hydraulic test was analyzed by means of chemical composition analysis, fracture analysis and microstructure examination.The results showed that the cracking reason was the casing tube organization distributed large inclusions, and its existence undermined the continuity of the materials organization and weakened transverse tensile strength, the stress concentration under the conditions of local stress exceeded the actual tensile strength.
中图分类号 TE931+.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/3/12
修改稿日期
网络出版日期
作者单位点击查看
备注赵大伟(1985-),男,硕士研究生。
引用该论文: ZHAO Da-wei,ZHAO Guo-xian,LI Ping-quan,LI Geng,XUE Yan. Cracking Reason Analysis of P110 Oil Casing after Hydraulic Test[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(1): 56～59
赵大伟,赵国仙,李平权,李 耿,薛 艳. P110石油套管水压试验开裂原因分析[J]. 理化检验－物理分册, 2010, 46(1): 56～59
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】DERS J, THIVARD B, GENTA A. Improvent of steel wire for cold heading[J]. Wire Joumal Intemational, 1992,10:73．
【2】樊立峰,项利,许学勇,等.中高牌号无取向硅钢的铸态组织及夹杂物形貌浅析[J]. 冶金丛刊, 2006(6): 1-3．
【3】战东平,张慧书,耿鑫,等.超低硫X65管线钢中非金属夹杂物研究[J]. 铸造技术, 2006,27(9): 906-909．
【4】尹宏斌,金山同.CAS工艺条件下钢包内夹杂物上浮规律的理论研究[J]. 钢铁,1995,30(10): 13-17．
【5】上海市机械制造工艺研究所.金相分析技术[M]. 上海: 上海科学技术文献出版社,1987．
【2】樊立峰,项利,许学勇,等.中高牌号无取向硅钢的铸态组织及夹杂物形貌浅析[J]. 冶金丛刊, 2006(6): 1-3．
【3】战东平,张慧书,耿鑫,等.超低硫X65管线钢中非金属夹杂物研究[J]. 铸造技术, 2006,27(9): 906-909．
【4】尹宏斌,金山同.CAS工艺条件下钢包内夹杂物上浮规律的理论研究[J]. 钢铁,1995,30(10): 13-17．
【5】上海市机械制造工艺研究所.金相分析技术[M]. 上海: 上海科学技术文献出版社,1987．
相关信息