40Mn2钢支撑辊淬火开裂分析
Quenching Cracking Analysis of 40Mn2 Steel Back-up Roll
摘 要
通过宏观检验、化学成分分析和金相检验等方法分析了40Mn2钢支撑辊淬火开裂的原因。结果表明：不合理的淬火工艺是造成支撑辊淬火开裂的主要原因，原始组织粗大进一步加剧了淬火开裂。最后提出了相应的改进措施。
支撑辊
淬火开裂
40Mn2 steel
back-up roll
quenching cracking
Abstract
By means of macroscopic examination, chemical composition analysis, metallographic examination and so on, the quenching cracking reason of back-up roll made with 40Mn2 steel was analyzed. The results showed that the unreasonable quenching process was main reason, and the coarse original microstructure accelerated quenching cracking. Finally, the improvement measures were put forward.
中图分类号 TH132
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/4/24
修改稿日期
网络出版日期
作者单位点击查看
备注余德河(1973-)，男，硕士研究生。
引用该论文: YU De-he. Quenching Cracking Analysis of 40Mn2 Steel Back-up Roll[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(9): 593～594
余德河. 40Mn2钢支撑辊淬火开裂分析[J]. 理化检验－物理分册, 2010, 46(9): 593～594
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴承建. 金属材料学[M]. 北京:冶金工业出版社,2000:38-45.
【2】张玉胜，刘雅政. 热轧冷却速率对微合金非调质钢34Mn2VN组织的影响[J]. 特殊钢，2006，27(6):24-26.
【2】张玉胜，刘雅政. 热轧冷却速率对微合金非调质钢34Mn2VN组织的影响[J]. 特殊钢，2006，27(6):24-26.
相关信息
| 标题 | 相关频次 | |
 | 42CrMo钢高强度螺栓轴向开裂失效分析 | 2 |
| 42CrMo钢蜗杆开裂原因分析 | 2 |
| 顶尖淬火开裂原因分析 | 2 |
| 列车缓冲器弹簧淬火开裂原因分析 | 2 |
| 45钢齿轮轴零件淬火开裂原因分析 | 1 |
| Q345R钢板卷筒过程的断裂分析 | 1 |
| 等角速万向节轴杆断裂原因分析 | 1 |