40CrNiMoA圆钢冲击功偏低原因分析
Reason Analysis on Low Impact Energy of 40CrNiMoA Steel Bar
摘 要
通过化学成分分析、力学性能测试和金相检验分析了某批40CrNiMoA圆钢冲击功偏低并呈现方向性的原因。结果表明:严重的带状组织偏析直接影响了材料的冲击功。通过分析带状组织的成因, 采取了等温退火工艺,从而有效控制了带状组织偏析,进而改善了冲击性能。
冲击功
带状组织
等温退火
40CrNiMoA steel
impact energy
banded structure
isothermal annealing
Abstract
Chemical composition, mechanical properties and microstructure were inspected to analyze the reason leading to impact property degradation and directivity of one batch 40CrNiMoA steel bars. The results showed that the banded structure in microstructure giving rises to the bad impact performance, and isothermal annealing was employed to eliminate banded structure for satisfying impact energy after analyze the reason of banded structure.
中图分类号 TG142.1+2 TG113.26+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2010/3/31
修改稿日期
网络出版日期
作者单位点击查看
备注田世英(1979-),男, 工学硕士。
引用该论文: TIAN Shi-ying,LIU Shi-liang,ZHENG Sheng-feng,MA Dun. Reason Analysis on Low Impact Energy of 40CrNiMoA Steel Bar[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2010, 46(11): 731～732
田世英,刘石亮,郑胜峰,马盾. 40CrNiMoA圆钢冲击功偏低原因分析[J]. 理化检验－物理分册, 2010, 46(11): 731～732
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】宋维锡. 金属学[M]. 北京: 冶金工业出版社, 1980.
【2】崔忠圻. 金属学与热处理[M]. 北京: 机械工业出版社, 2000.
【2】崔忠圻. 金属学与热处理[M]. 北京: 机械工业出版社, 2000.
相关信息