钢轨踏面掉块原因分析
Reason Analysis of Peeling on Rail Tread
摘 要
U71Mn (60 kg/m)钢轨铺设在主干线与车站进出口联接处使用50多d(天)后出现踏面掉块。采用化学成分分析、宏观和微观检验等方法分析其掉块原因。结果表明：列车高速运行时突遇偶发事故而采用紧急制动措施,强大的制动力造成列车车轮与钢轨踏面之间的摩擦致使该区域突然升温而后又降温,进而发生相变生成马氏体并形成裂纹。随后在车轮的反复碾压作用下最终造成钢轨踏面掉块。
踏面掉块
马氏体
裂纹
rail
tread peeling
martersite
crack
Abstract
The U71Mn rail,whose type was 60 kg/m,had been laid in the joint of main line and the station port for more than 50 days and peeled on the rail tread. The reason was analyzed by means of chemical composition analysis,macrostructure and microstructure examination etc. The results showed that,when the train ran rapidly,suddenly the contingency happened,the driver adopted the emergency brake scheme to avoiding danger,then the powerful brake force had caused the wheel and the rail to contact abruptly and closely,at the same time,the large friction was generated to cause the crack,and the phase change to generate the martersite was happened in rail tread by high temperature. The crack and martersite had been rolled repeatedly by wheel,finally,the peeling happened on the rail tread.
中图分类号 U213.4+2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/9/27
修改稿日期
网络出版日期
作者单位点击查看
备注吴雄先(1951-),男,高级工程师。
引用该论文: WU Xiong-xian,DENG Jian-hui,WANG Fei-long. Reason Analysis of Peeling on Rail Tread[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 39～40
吴雄先,邓建辉,王飞龙. 钢轨踏面掉块原因分析[J]. 理化检验－物理分册, 2009, 45(1): 39～40
被引情况:
【1】李闯,刘丰收,俞喆,梁旭,张银花,周清跃, "某高速铁路钢轨踏面伤损原因分析",理化检验－物理分册 51, 894-897(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】铁道科学研究院金化所. 钢轨伤损图谱[M].北京: 中国铁道出版社,1992:66-70．
相关信息