自行车链轮曲柄断裂原因分析
Fracture Reason Analysis of the Chain Wheel Brace of Bicycle
摘 要
采用化学成分分析、微观组织检验、断口宏观和微观观察及能谱分析等方法对自行车链轮曲柄断裂的原因进行了分析。结果表明:曲柄断裂为疲劳断裂;由于材料的过烧,使晶界上产生复熔共晶球,脆化了材料的晶界,使用时产生沿晶裂纹,降低了材料的疲劳强度,致使曲柄产生早期疲劳失效断裂。
曲柄
断裂
复熔共晶球
疲劳
bicycle
brace
fracture
remelting eutectic
fatigue
Abstract
By means of chemical composition analysis,microstructure examination,macro-micro fracture examination and EDS analysis,the fracture reason of chain wheel brace of bicycle was analyzed. The result showed that because of the overheated,there were remelting eutectic on grain boundaries,which embrittled them,and cracks emerged when used,which lower the fatigue resistance of the material,and led to premature fatigue failure.
中图分类号 U484
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/11/7
修改稿日期
网络出版日期
作者单位点击查看
备注王明福(1978-),男,工程师,硕士。
引用该论文: WANG Ming-fu,LI Xiao-ling,FEI Qin-yong. Fracture Reason Analysis of the Chain Wheel Brace of Bicycle[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 53～54
王明福,李晓玲,费勤勇. 自行车链轮曲柄断裂原因分析[J]. 理化检验－物理分册, 2009, 45(1): 53～54
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉.金属材料金相图谱[M].北京：机械工业出版社,2006．
【2】廖景娱.金属构件失效分析[M].北京：化学工业出版社,2003．
【2】廖景娱.金属构件失效分析[M].北京：化学工业出版社,2003．
相关信息
| 标题 | 相关频次 | |
 | 注水阀弹簧断裂原因分析 | 6 |
| 60Si2CrA热轧弹簧断裂失效分析 | 4 |
| N80油管断裂分析 | 4 |
| 扳手连接件表面黑点原因分析 | 4 |
| 抽油泵凡尔罩断裂失效分析 | 4 |
| 储液筒吸气管断裂分析 | 4 |
| 传输装置转子转轴断裂原因分析 | 4 |
| 船用艉轴断裂失效分析 | 4 |
| 电厂外供泵轴断裂原因分析 | 4 |
| 电站连接螺栓断裂失效分析 | 4 |
| 动力站碱液输送泵泵轴断裂原因分析 | 4 |
| 分动箱齿轮断裂原因 | 4 |
| 高压调节阀后热电偶套管断裂原因分析 | 4 |
| 列车车轮辐板断裂原因分析 | 4 |
| 某HL级35CrMo抽油杆断裂原因分析 | 4 |
| 某超临界电站锅炉送风机叶片的断裂原因分析 | 4 |
| 某挖掘机高强螺栓断裂原因分析 | 4 |
| 凝结水泵轴断裂原因分析 | 4 |
| 起重机轴承失效分析 | 4 |
| 汽车冷却装置护板断裂的原因 | 4 |
| 汽轮机末级叶片断裂原因分析 | 4 |
| 切胶机连接轴断裂原因分析 | 4 |
| 钛合金杆端体断裂原因 | 4 |
| 压缩机连杆断裂失效分析 | 4 |
| 造船龙门起重机车轮轴断裂原因分析 | 4 |
| 中压调节阀油动机活塞杆断裂分析 | 4 |
| 自动扶梯扶手驱动轴断裂原因分析 | 4 |
| 钻柱转换接头断裂原因分析 | 4 |
| 镍钛丝断裂原因分析 | 3 |
| 镍钛丝断裂原因分析 | 3 |