N80钢管残余应力的测试与分析
Measurement and Analysis of Residual Stresses in N80 Steel Pipe
摘 要
采用全释放法测试N80钢管的残余应力，结果发现:无论是直管还是发生变形的弯管在它们的同一部位，其内表面与外表面的残余应力是不均匀的，而且沿内圆周或是外圆周其残余应力的分布也不均匀。得出高的残余应力加上分布的不均匀性是钢管发生弯曲变形的主要原因之一。
N80钢管
全释放法
residual stress
N80 steel pipe
section method
Abstract
It was found that both of longitudinal residual stresses and circumferential residual stresses in the same position of undeformed N80 steel pipe and deformed N80 steel pipe were not of uniformity in viewpoint of measuring results by section method. The results showed that the main deformation reason was high residual stress and its asymmetrical distribution.
中图分类号 TG113.25 TG392
所属栏目 实践经验
基金项目
收稿日期 2007/12/6
修改稿日期
网络出版日期
作者单位点击查看
备注李荣锋(1966-),男,教授级高工,博士。
引用该论文: LI Rong-feng,ZHU Hong-chuan,LI Chang-yi,LI Fu-lin. Measurement and Analysis of Residual Stresses in N80 Steel Pipe[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(1): 65～66
李荣锋,祝洪川,李长一,李福林. N80钢管残余应力的测试与分析[J]. 理化检验－物理分册, 2009, 45(1): 65～66
被引情况:
【1】龚丹梅,余世杰,刘贤文,魏立明,马金山,袁鹏斌, "定向钻穿越S135钢级钻杆的断裂分析",机械工程材料 38, 104-108(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Michael Law. Neutron residual stress measurements in line pipe[J]. Physica B,2006(385/386):900-903．．
【2】徐 勇,程先华.P110套管冷矫残余应力模拟分析[J]. 钢铁,2004,39(1):30．
【3】李连进,王惠斌.石油管定径轧制残余应力的模拟分析[J]. 钢铁研究学报,2007,19(1):31．
【2】徐 勇,程先华.P110套管冷矫残余应力模拟分析[J]. 钢铁,2004,39(1):30．
【3】李连进,王惠斌.石油管定径轧制残余应力的模拟分析[J]. 钢铁研究学报,2007,19(1):31．
相关信息