16 t大型热模锻锤锤杆断裂原因分析
Failure Analysis of 16 t Heavy-duty Drop Hammer Rod
摘 要
大型模锻锤杆在锻击机车传动盘时连续出现早期断裂。采用化学成分分析、锤杆表面磨损现象分析、宏观断口分析、硬度检测和显微组织分析等方法,并结合锻造工艺对断裂锤杆进行了综合分析。结果表明:由于锤杆的硬度参数选择偏低,制造过程中存在一定的组织缺陷，同时由于锤杆恶劣的受力条件，导致锤杆在使用过程中出现粘着磨损疲劳断裂。
锤杆
粘着磨损
疲劳断裂
16 t heavy-duty die forging hammer
hammer rod
agglutinate abrasion
fatigue failure
Abstract
Early and continuous fatigue failure of 16 t heavy-duty drop hammer rods happened in forging transmission pan,and fracture reasons were analyzed by means of chemical compositions analysis,surface abrasion test and macro fracture analysis,hardness measurement,metallographic examination,and combining with forging technical process.The results shows that agglutionate fatigue failure were resulted from illogical hardness parameters,microstructure defect and bad stress condition.
中图分类号 TG315.3+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/7/25
修改稿日期
网络出版日期
作者单位点击查看
备注程 里(1962-),男,教授级高级工程师。
引用该论文: CHENG Li,YANG Ping. Failure Analysis of 16 t Heavy-duty Drop Hammer Rod[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(2): 114～117
程里,杨萍. 16 t大型热模锻锤锤杆断裂原因分析[J]. 理化检验－物理分册, 2009, 45(2): 114～117
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王仲仁. 锻压手册（锻造 第3卷）[M]. 北京：机械工业出版社,2002．
【2】上海交通大学《金属断口分析》编写组. 金属断口分析[M]. 北京：国防工业出版社,1979．
【3】程 里. 大型模锻锤锤杆疲劳宏观断口分析实例[J]. 理化检验-物理分册,2007,43(5): 239-241．
【4】锻工手册编写组.锻工手册 [M]. 北京：机械工业出版社,1976．
【5】李永堂.锻压设备理论与控制[M]. 北京：国防工业出版社，2005．
【6】夏琴香. 模锻锤锤杆动态特性的研究[J]. 西北工业大学学报，1993(4):504-509．
【2】上海交通大学《金属断口分析》编写组. 金属断口分析[M]. 北京：国防工业出版社,1979．
【3】程 里. 大型模锻锤锤杆疲劳宏观断口分析实例[J]. 理化检验-物理分册,2007,43(5): 239-241．
【4】锻工手册编写组.锻工手册 [M]. 北京：机械工业出版社,1976．
【5】李永堂.锻压设备理论与控制[M]. 北京：国防工业出版社，2005．
【6】夏琴香. 模锻锤锤杆动态特性的研究[J]. 西北工业大学学报，1993(4):504-509．
相关信息