高强度螺栓断裂原因分析
Fracture Analysis on High Strength Blot
摘 要
表面磷化处理的高强度螺栓在装配时发生断裂。对断裂螺栓进行宏观和微观检验、化学成分分析、金相检验、能谱分析和力学性能分析。结果表明: 该螺栓的裂纹表面有氧化物且存在与螺栓表面相似的磷化物,裂纹处没有脱碳现象,说明裂纹在磷化处理前已存在,判断该裂纹是淬火裂纹。螺栓的断裂是由淬火裂纹造成的。
磷化
淬火裂纹
high strength bolt
parkerizing
quenching crack
Abstract
The parkerizing high strength blot fractured during assembly. The analysis on macro and micro,chemical composition,metallographic,EDAS and mechanical property were carried out on the fractured blot. The results showed that the crack surface of blot was oxidized and phosphate similar with bolt surface existed on the crack surface,and there was no decarbonization layer on crack,which showed that the crack existed before parkerizing,so the crack was quenching crack. The bolt fractured was caused by quenching crack.
中图分类号 TH131
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/11/25
修改稿日期
网络出版日期
作者单位点击查看
备注陈华锋(1983-),男,硕士研究生。
引用该论文: CHEN Hua-feng,WANG Rong,WANG Bin,BA Fa-hai. Fracture Analysis on High Strength Blot[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(4): 224～227
陈华锋,王 荣,王 滨,巴发海. 高强度螺栓断裂原因分析[J]. 理化检验－物理分册, 2009, 45(4): 224～227
被引情况:
【1】王 荣, "10.9级高强度螺钉断裂分析",理化检验－物理分册 46, 263-266(2010)
【2】周艳,张洁, "高强度螺栓断裂原因分析",理化检验－物理分册 50, 526-527(2014)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘柯军,徐香秋,苏瑛. 淬火裂纹分类讨论[J]. 理化检验-物理分册,2005,41(3):108-111．
【2】机械工业理化检验人员技术培训和资格鉴定委员会.金相检验[M]. 上海: 上海科学普及出版社,2006:249-253．
【2】机械工业理化检验人员技术培训和资格鉴定委员会.金相检验[M]. 上海: 上海科学普及出版社,2006:249-253．
相关信息