X70管线钢焊接接头热影响区的冲击性能
Impact Property of Heat-affected Zone in Welded Joint of X70 Pipeline Steel
摘 要
对X70管线钢焊接接头热影响区进行了冲击试验，对结果进行了分析。结果表明:X70管线钢焊接接头热影响区冲击试样的冲击功与断口剪切面积基本成线性比例关系，冲击功越高,剪切面积越大。焊接接头热影响区冲击试样的断口由韧性区、脆性区和韧脆混合区组成。脆性区为解理断裂,韧脆混合区为准解理断裂。
冲击功
剪切面积
解理断裂
准解理断裂
X70 pipeline steel
impact work
shearing area
cleavage fracture
quasi-cleavage fracture
Abstract
Impact test results of heat-affected zone in welded joint of X70 pipeline steel were studied. The results indicated that impact absorbed energy of heat-affected zone in welded joint of X70 pipeline steel were proportional with shearing area on the whole. Impact absorbed energy was higher,shearing area was bigger. Impact fracture surface of heat-affected zone in welded joint included tough zone ,brittle zone and tough-brittle zone. Brittle zone was cleavage fracture,tough-brittle zone was quasi-cleavage fracture.
中图分类号 TG113.2
所属栏目 试验与研究
基金项目
收稿日期 2008/10/8
修改稿日期
网络出版日期
作者单位点击查看
备注蔺卫平(1975-),女,工程师,硕士。
引用该论文: LIN Wei-ping,LI Ai-ping,WANG Xiao-yan,LI Na,WANG Ya-long,REN Ji-cheng. Impact Property of Heat-affected Zone in Welded Joint of X70 Pipeline Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(5): 273～276
蔺卫平,李爱萍,王晓燕,李 娜,王亚龙,任继承. X70管线钢焊接接头热影响区的冲击性能[J]. 理化检验－物理分册, 2009, 45(5): 273～276
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】郑磊,高珊.西气东输工程大口径X70输气管线用板卷的研制[J]. 钢铁研究学报,2006,18(3)：46-50．
【2】辛希贤. 管线钢的焊接[M]. 西安：陕西科技出版社,1997．
【3】熊庆人,高惠临,霍春勇. X80管线钢焊接热影响区的韧性[J]. 机械工程材料,2007,31(4)：29-33．
【4】崔约贤,王长利. 金属断口分析[M]. 哈尔滨：哈尔滨工业大学出版社,1998．
【2】辛希贤. 管线钢的焊接[M]. 西安：陕西科技出版社,1997．
【3】熊庆人,高惠临,霍春勇. X80管线钢焊接热影响区的韧性[J]. 机械工程材料,2007,31(4)：29-33．
【4】崔约贤,王长利. 金属断口分析[M]. 哈尔滨：哈尔滨工业大学出版社,1998．
相关信息