1Cr18Ni9Ti钢炉管开裂原因分析
Analysis on Cracking Reason of 1Cr18Ni9Ti Steel Furnace Tube
摘 要
采用金相检验、力学性能试验、铁磁相含量测定、断口及能谱分析等方法对1Cr18Ni9Ti钢炉管的开裂原因进行分析。结果表明：开裂炉管的内壁裂纹为连多硫酸应力腐蚀开裂,而外壁裂纹为硫化物促进下的氯化物应力腐蚀开裂。并提出了预防炉管开裂的建议。
炉管
连多硫酸
应力腐蚀开裂
1Cr18Ni9Ti steel
furnace tube
PTA
stress corrosion cracking
Abstract
The cracking reason of 1Cr18Ni9Ti steel furnace tube was analyzed by metallographic examination,mechanical performance test,ferrimagnetic phase content measurement,fractograph and EDS analysis etc. The results showed that there were PTA stress corrosion cracking on furnace tube inside wall and there were some stress corrosion cracking which was promoted by sulphide on furnace pipe outside wall. The proposal for avoiding cracking had been given.
中图分类号 TE963
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/3/4
修改稿日期
网络出版日期
作者单位点击查看
备注李蓉蓉(1959-),女,高级工程师。
引用该论文: LI Rong-rong,LI Ping-jin. Analysis on Cracking Reason of 1Cr18Ni9Ti Steel Furnace Tube[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(5): 292～298
李蓉蓉,李平瑾. 1Cr18Ni9Ti钢炉管开裂原因分析[J]. 理化检验－物理分册, 2009, 45(5): 292～298
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】肖纪美. 不锈钢的金属学问题[M]. 北京：冶金工业出版社,1983．
【2】李平瑾,吕容运. 渣油加氢汽油管线的开裂成因分析[J]. 中国锅炉压力容器安全,2000,16(5):27-31．
【3】小若正伦. 金属的腐蚀破坏与防蚀技术[M].袁宝林,过家驹,朱应杨,译.北京：化学工业出版社,1988．
【2】李平瑾,吕容运. 渣油加氢汽油管线的开裂成因分析[J]. 中国锅炉压力容器安全,2000,16(5):27-31．
【3】小若正伦. 金属的腐蚀破坏与防蚀技术[M].袁宝林,过家驹,朱应杨,译.北京：化学工业出版社,1988．
相关信息