锰、铜含量对锌铝合金组织与性能的影响
Effect of Mn and Cu Content on Microstructure and Properties of Zn-Al Alloys
摘 要
研究了不同含量的锰和铜对锌铝合金的组织与力学性能的影响。结果表明：锰和铜含量较低时,对合金的力学性能无显著影响;随着锰和铜含量的升高,合金的硬度大幅提高,冲击韧度基本不变。
组织
硬度
冲击韧度
Zn-Al alloy
microstructure
hardness
impact toughness
Abstract
Effect on mechanical property and microstructure of Zn-Al alloys added different content Mn and Cu were studied. The results showed that the mechanical property of Zn-Al alloy was no effect notably under adding a samll content Mn and Cu. With the increasing of Mn and Cu content in the alloys,the hardness of the alloys had increased greatly,and the impact toughness of the alloys did not almost change.
中图分类号 TG146.1
所属栏目 试验与研究
基金项目
收稿日期 2008/10/9
修改稿日期
网络出版日期
作者单位点击查看
备注李建春(1976-),男,工程师。
引用该论文: LI Jian-chun. Effect of Mn and Cu Content on Microstructure and Properties of Zn-Al Alloys[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(6): 331～334
李建春. 锰、铜含量对锌铝合金组织与性能的影响[J]. 理化检验－物理分册, 2009, 45(6): 331～334
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】蔡强. 锌合金[M]. 长沙: 中南工业大学出版社,1987．
【2】赵浩锋,王玲. 铸造锌合金及其复合材料[M]. 北京: 中国标准出版社,2002:14．
【3】李建春,郝兴明,卫爱丽,等. 镁元素对锌基合金显微组织与性能的影响[J]. 热加工工艺,2008(6):38-39．
【2】赵浩锋,王玲. 铸造锌合金及其复合材料[M]. 北京: 中国标准出版社,2002:14．
【3】李建春,郝兴明,卫爱丽,等. 镁元素对锌基合金显微组织与性能的影响[J]. 热加工工艺,2008(6):38-39．
相关信息