X射线衍射法测定材料织构的参数探讨
Parameter Exploration of Testing Material Texture by X-ray Diffraction
摘 要
通过调节管电流的大小和有无滤波片来探讨测定参数对材料织构的影响。结果表明：管电流的大小对织构测定基本没有影响，而去掉滤波片后主要织构组分没有变化，但最大极密度降低，弱织构组分能够显现。
管电流
滤波片
orientation distribution function
the current of the X-ray tube
filter
Abstract
The parameter of testing texture such as the current of the X-ray tube and filter were considered. The results showed that the current of X-ray tube had no effect with the texture. Comparing with results which testing with the filter,the main texture did not change,the highest pole densities lower and the weak texture could be found without filter.
中图分类号 TG115.22
所属栏目 试验技术与方法
基金项目
收稿日期 2008/8/26
修改稿日期
网络出版日期
作者单位点击查看
备注王 锐(1964-),男,高级工程师。
引用该论文: WANG Rui,ZHOU Jing,LI Wen-zhu,HUANG Lei. Parameter Exploration of Testing Material Texture by X-ray Diffraction[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(6): 348～350
王锐,周敬,李文竹,黄磊. X射线衍射法测定材料织构的参数探讨[J]. 理化检验－物理分册, 2009, 45(6): 348～350
被引情况:
【1】王德宝,王 越, "高强IF钢板沿厚度方向的织构和显微组织",理化检验－物理分册 46, 348-351(2010)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】梁志德,徐家桢,王福. 织构材料的三维取向分析术[M]. 沈阳: 东北工学院出版社,1986:16-19．
【2】毛卫民. 金属材料的晶体学织构与各相异性[M]. 北京: 科学出版社，2002：4-6．
【3】李树棠. 晶体X射线衍射学基础[M]. 北京: 冶金工业出版社,1990:11-16．
【4】丘利,胡玉和. X射线衍射技术及设备[M]. 北京: 冶金工业出版社,2001:189-198．
【2】毛卫民. 金属材料的晶体学织构与各相异性[M]. 北京: 科学出版社，2002：4-6．
【3】李树棠. 晶体X射线衍射学基础[M]. 北京: 冶金工业出版社,1990:11-16．
【4】丘利,胡玉和. X射线衍射技术及设备[M]. 北京: 冶金工业出版社,2001:189-198．
相关信息