变形铝合金显微组织阳极复膜显示技术
Microstructure Display Technology on Distortion Aluminum Alloy by Anodic Film Formation
摘 要
介绍了显示7050铝合金显微组织的两组电解抛光+阳极复膜工艺,并作了比较。结果表明:采用HBF4水溶液作制膜液的工艺对显示铝合金变形织构效果更好。
阳极复膜
显微组织
aluminum alloy
anodic film formation
microstructure
Abstract
Two groups of processing parameters about electro polishing and anodic film formation applied to distortion aluminum alloy for optical analysis were described. The result showed that the process which chose HBF4 as anodic film formation component was better to show the texture of distortion aluminum alloy.
中图分类号 TG146.2
所属栏目 试验技术与方法
基金项目 广东省教育部产学研结合项目(2008B090500084)
收稿日期 2008/10/20
修改稿日期
网络出版日期
作者单位点击查看
备注麦永津(1984-),男,硕士研究生。
引用该论文: MAI Yong-jin,JIE Xiao-hua,ZHENG Xiang-xin,YU Neng. Microstructure Display Technology on Distortion Aluminum Alloy by Anodic Film Formation[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(9): 546～548
麦永津,揭晓华,郑向新,于 能. 变形铝合金显微组织阳极复膜显示技术[J]. 理化检验－物理分册, 2009, 45(9): 546～548
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 3246-1982 铝及铝合金加工制品显微组织检验方法[S]．
【2】谭澄宇,郑子樵. 阳极复膜法制备铝箔金相试样及组织观察[J]. 理化检验-物理分册,2000,36(7): 308-309．
【3】张小平,秦建平. 轧制理论[M].北京: 冶金工业出版社,2006: 132-133．
【2】谭澄宇,郑子樵. 阳极复膜法制备铝箔金相试样及组织观察[J]. 理化检验-物理分册,2000,36(7): 308-309．
【3】张小平,秦建平. 轧制理论[M].北京: 冶金工业出版社,2006: 132-133．
相关信息