摘 要
根据JJF 1059-1999标准,分析了S355J2+N钢板在拉伸试验过程中设备、量具、试验人员、数值修约等因素对试验结果的影响,并对其进行了不确定度评定。结果为: Urel(ReL)=0.9%,Urel(Rm)=0.9%,Urel(A)=0.4%;表明S355J2+N钢板的拉伸检测过程受控正常。
Abstract
According to JJF 1059-1999,every factor of S355J2+N steel plate had been tested. Calculating the effects of different factors such as equipment,measuring tool,operator,rounding of numberical values,and the uncertainty of testing was also analyzed,the result of the relative measurement uncertainty was Urel(ReL)=0.9%,Urel(Rm)=0.9%,Urel(A)=0.4%. It was shown that the tensile test procedures were under control normally.
中图分类号 O213.2
所属栏目 试验技术与方法
基金项目
收稿日期 2008/12/19
修改稿日期
网络出版日期
作者单位点击查看
备注叶君龙(1984-),男,助理工程师,学士。
引用该论文: YE Jun-long,SHU Xian-qing,ZHANG Hua. Uncertainty Evaluation of Tensile Test Result for S355J2+N Steel Plate[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(9): 549~552
叶君龙,舒先庆,张 华. S355J2+N钢板拉伸试验测量结果的不确定度评定[J]. 理化检验-物理分册, 2009, 45(9): 549~552
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】JJF 1059-1999 测量不确定度评定与表示[S].
【2】王承忠.测量不确定度原理在理化检验中的应用[J]. 理化检验-物理分册,2003,39(1-7): 57,113,167,220,275,328,382.王承忠.测量不确定度原理在理化检验中的应用[J]. 理化检验-物理分册,2003,39(1-7): 57,113,167,220,275,328,382.
【3】王承忠.材料理化检验测量不确定度评定方法的研究[J].理化检验-物理分册,2007,43(6): 282-286.
【2】王承忠.测量不确定度原理在理化检验中的应用[J]. 理化检验-物理分册,2003,39(1-7): 57,113,167,220,275,328,382.王承忠.测量不确定度原理在理化检验中的应用[J]. 理化检验-物理分册,2003,39(1-7): 57,113,167,220,275,328,382.
【3】王承忠.材料理化检验测量不确定度评定方法的研究[J].理化检验-物理分册,2007,43(6): 282-286.
相关信息