Leakage Reason Analysis in Cylinder of Tower D210
摘 要
采用化学成分分析、金相检验和断口分析等方法,对304L钢D210塔筒体泄漏原因进行了分析。结果表明:D210塔筒体泄漏原因是由于氯离子的存在而产生应力腐蚀开裂所致。由于敏感材料、应力腐蚀环境及应力三个条件共同存在,在一定温度下使其产生应力腐蚀裂纹,裂纹起始于筒体外壁角焊缝处,而后向内壁扩展,最终穿透筒壁,致使该塔筒体在角焊缝处产生破裂泄漏。
Abstract
The leakage reason in cylinder of the tower D210 was analyzed by chemical composition analysis,metallographic examination and fracture analysis. The analysis result showed that the leakage was caused by stress corrosion cracking which resulted from existing chloride ion. Under the certain temperature,stress corrosion crack produced at the combined effect conditions of sensitive materials,stress corrosion circumstance and tensile stress. The crack,which initiating in fillet weld on outer cylinder,extended to the wall and eventually penetrated the tube wall. Then towers cylinder leaked on the fillet weld.
中图分类号 TQ053.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/6/17
修改稿日期
网络出版日期
作者单位点击查看
备注钱耀洲(1965-),男,工程师。
引用该论文: QIAN Yao-zhou,YOU Ju. Leakage Reason Analysis in Cylinder of Tower D210[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(9): 570~572
钱耀洲,游 菊. D210塔筒体泄漏原因分析[J]. 理化检验-物理分册, 2009, 45(9): 570~572
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王荣. 不锈钢换热器泄漏原因分析[J]. 理化检验-物理分册,2006,41(5):255-257.
【2】陆世英,王欣增,李不钟.不锈钢应力腐蚀事故分析与耐应力腐蚀不锈钢[M]. 北京:原子能出版社,1992.
【3】上海交通大学《金相分析》编写组. 金相分析[M]. 北京: 国防工业出版社,1982.
【2】陆世英,王欣增,李不钟.不锈钢应力腐蚀事故分析与耐应力腐蚀不锈钢[M]. 北京:原子能出版社,1992.
【3】上海交通大学《金相分析》编写组. 金相分析[M]. 北京: 国防工业出版社,1982.
相关信息