S135钻杆断裂原因分析
Cracking Reason Analysis of S135 Drill Pine
摘 要
通过化学成分分析、力学性能测试、显微组织分析等手段对某断裂失效的S135钻杆进行了材质理化检验;采用SEM和EDS分别对断口形貌及表面腐蚀产物成分进行了分析。结果表明：该钻杆的材料性能符合API Spec SD规范要求,钻杆断裂的主要原因是硫化氢应力腐蚀开裂,并伴有一定程度的二氧化碳腐蚀。
硫化氢应力腐蚀开裂
二氧化碳腐蚀
drill pine
sulfide stress corrosion cracking
CO2 corrosion
Abstract
Material property of S135 drill pine were tested by means of chemical compositions analysis,mechanical property test and metallographic examination. Fracture suface morphology and corrosion production composition were analyzed by SEM and EDS respectively. The results show that the material properties accorded to the requirement of API SPEC 5D standard and the main reason of cracking was sulfide stress corrosion cracking (SSCC) accompanied by CO2 corrosion.
中图分类号 TE921+.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/1/12
修改稿日期
网络出版日期
作者单位点击查看
备注蔡 锐(1983-),男,工程师，硕士。
引用该论文: CAI Rui,HU Zhi-bing,TIAN Wei,LI Li-feng,LI Fa-gen. Cracking Reason Analysis of S135 Drill Pine[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(10): 645～648
蔡 锐1,胡志兵2,田 伟1,李丽锋1,李发根1. S135钻杆断裂原因分析[J]. 理化检验－物理分册, 2009, 45(10): 645～648
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李宏江. 油田生产中硫化氢的危害及防护[J]. 安全技术,2008,8(7):21-23．
【2】李鹤林,李平全,冯耀荣. 石油钻柱失效分析及预防措施[M]. 北京: 石油工业出版社,1999: 196-200．
【3】毕海斌. H2S 应力腐蚀的影响因素及预防措施[J]. 甘肃科技,2008,24(7):65-67．
【2】李鹤林,李平全,冯耀荣. 石油钻柱失效分析及预防措施[M]. 北京: 石油工业出版社,1999: 196-200．
【3】毕海斌. H2S 应力腐蚀的影响因素及预防措施[J]. 甘肃科技,2008,24(7):65-67．
相关信息