SKD61钢压铸模具开裂分析
Cracking Analysis of Die Casting Mould of SKD61 Steel
摘 要
通过化学成分分析、力学性能测试、金相检验以及断口分析等方法对SKD61钢压铸模具开裂原因进行分析。结果表明:由于该模具材料的钼和钒含量偏低,导致热处理后的硬度偏低,使得疲劳强度降低,从而在服役中以疲劳形式早期开裂失效。
压铸模具
开裂
疲劳
SKD61 steel
die casting mould
cracking
fatigue
Abstract
The cracking causes of the die casting mould of SKD61 steel were analyzed by chemical composition analysis,mechanical property testing,microstructure examination and fracture analysis. The results showed that the lower contents of molybdenum and vanadium in the mould material resulted in the lower hardness after heat treatment,then resulted in the lower fatigue strength was the main reason causing the mould fatigue fracture.
中图分类号 TG241
所属栏目 质量控制与失效分析
基金项目
收稿日期 2009/4/23
修改稿日期
网络出版日期
作者单位点击查看
备注王春亮(1978-),男,工程师,硕士。
引用该论文: WANG Chun-liang,LU Hui,LIU Le,LI Ling. Cracking Analysis of Die Casting Mould of SKD61 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2009, 45(11): 703～706
王春亮,陆 慧,刘 乐,李 玲. SKD61钢压铸模具开裂分析[J]. 理化检验－物理分册, 2009, 45(11): 703～706
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】JJS G4404-2006 合金工具钢[S]．
【2】蔡宏伟.金相检验[M].北京：中国计量出版社,2008:24-25．
【3】元清,李德林,元涛,等.SKD61钢模具早期失效原因分析[J].兵器材料科学和工程,2004,27(6):58-61．
【4】唐汝钧.机械工程材料测试手册(物理金相卷)[M].沈阳：辽宁科学技术出版社,1999:825-842．
【5】王春亮,杨力.齿轮的失效分析[J].理化检验-物理分册,2007,43(7):366-369．
【6】梁思祖,梁耀能,李茅坪. H13钢铝合金压铸模开裂原因分析[J]. 金属热处理,2007,27(12):48-50．
【2】蔡宏伟.金相检验[M].北京：中国计量出版社,2008:24-25．
【3】元清,李德林,元涛,等.SKD61钢模具早期失效原因分析[J].兵器材料科学和工程,2004,27(6):58-61．
【4】唐汝钧.机械工程材料测试手册(物理金相卷)[M].沈阳：辽宁科学技术出版社,1999:825-842．
【5】王春亮,杨力.齿轮的失效分析[J].理化检验-物理分册,2007,43(7):366-369．
【6】梁思祖,梁耀能,李茅坪. H13钢铝合金压铸模开裂原因分析[J]. 金属热处理,2007,27(12):48-50．
相关信息